Abstract:We studied the structural and compositional transformations of colloidal covellite (CuS) nanocrystals (and of djurleite (Cu1.94S) nanocrystals as a control) when exposed to divalent cations, as Cd2+ and Hg2+, at room temperature in organic solvents. All the experiments were run in the absence of phosphines, which are a necessary ingredient for cation exchange reactions involving copper chalcogenides, as they strongly bind to the expelled Cu+ ions. Under these experimental conditions, no remarkable reactivity was indeed seen for both CuS and Cu1.94S nanocrystals. On the other hand, in the covellite structure 2/3 of sulfur atoms form covalent S–S bonds. This peculiarity suggests that the combined presence of electron donors and of foreign metal cations can trigger the entry of both electrons and cations in the covellite lattice, causing reorganization of the anion framework due to the rupture of the S–S bonds. In Cu1.94S, which lacks S–S bonds, this mechanism should not be accessible. This hypothesis was proven by the experimental evidence that adding ascorbic acid increased the fraction of metal ions incorporated in the covellite nanocrystals, while it had no noticeable effect on the Cu1.94S ones. Once inside the covellite particles, Cd2+ and Hg2+ cations engaged in exchange reactions, pushing the expelled Cu+ ions toward the not-yet exchanged regions in the same particles, or out to the solution, from where they could be recaptured by other covellite nanoparticles/domains. Because no good solvating agent for Cu ions was present in solution, they essentially remained in the nanocrystals.

Controlled synthesis and characterization of covellite (CuS) nanoflakes

Shape-controlled Synthesis and Self-Assembly of Hexagonal Covellite (cus) Nanoplatelets.

Copper Sulfide Nanocrystals with Tunable Composition by Reduction of Covellite Nanocrystals with Cu+ Ions.

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

Controllable Synthesis of Monodisperse CuS Nanocrystals

Controllable Synthesis of Cu<sub>2</sub>S Nanocrystals and Their Assembly into a Superlattice

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

The Size Controlled Synthesis and Self-Assembled of Monodisperse Cu2S Nanocrystals

A chemically-induced, room temperature, single source precursor to CuS (covellite) nanomaterials: Synthesis and reactivity of [Cu(S2CNHBz)]n

Synthesis of Hierarchical CuS Flower-Like Submicrospheres Via an Ionic Liquid-Assisted Route

Nanoscale Transformations in Covellite (cus) Nanocrystals in the Presence of Divalent Metal Cations in a Mild Reducing Environment.

Controllable Transformation from Rhombohedral Cu1.8S Nanocrystals to Hexagonal CuS Clusters: Phase- and Composition-Dependent Plasmonic Properties

Controllable Synthesis of CuS Nanostructures from Self-Assembled Precursors with Biomolecule Assistance

Studies of synthesis and optical properties of ZnS nanocrystals

Facile Synthesis of Leaf-like Cu(OH)2 and Its Conversion into CuO with Nanopores

Synthesis and Characterization of SnS Nanoflakes

Controlled growth of Cu2S hexagonal microdisks and their optical properties

Unconventional 0-, 1-, and 2-Dimensional Single-Crystalline Copper Sulfide Nanostructures

Colloidal Synthesis of Uniform CuI Nanoparticles and Their Size Dependent Optical Properties

Shape-controlled synthesis of copper sulfide nanocrystals via a soft solution route

Copper sulfide nanosheets with shape-tunable plasmonic properties in the NIR