Abstract:The nucleation and growth of colloidal CdSe nanocrystals with a variety of elongated shapes were explored in detail. The critical size nuclei for the system were magic sized nanoclusters, which possessed a sharp and dominated absorption peak at 349 nm. The formation of the unique magic sized nuclei in a broad monomer concentration range was not expected by the classic nucleation theory. We propose that this was a result of the extremely high chemical potential environment, that is, very high monomer concentrations in the solution, required for the growth of those elongated nanocrystals. The shape, size, and size/shape distributions of the resulting nanocrystals were all determined by two related factors, the magic sized nuclei and the concentration of the remaining monomers after the initial nucleation stage. Without any size sorting, nearly monodisperse CdSe quantum structures with different shapes were reproducibly synthesized by using the alternative cadmium precursors, cadmium-phosphonic acid complexes. A reasonably large excess of the cadmium precursor, which is less reactive than the Se precursor, was found beneficial for the system to reach the desired balance between nucleation and growth. The shape evolution and growth kinetics of these elongated nanocrystals were consistent with the diffusion-controlled model proposed previously. The branched nanocrystals had to grow at very high monomer concentrations because the multiple growth centers at the end of each branch must be fed with a very high diffusion flux to keep all branches in the 1D-growth mode. The rice-shaped nanocrystals were found as special products of the 3D-growth stage. The growth of the nanocrystals in the 1D-growth stage was proven to be not unidirectional after the length of the nanocrystals reached a certain threshold. Experimental results indicate that coordinating solvents and two ligands with distinguishable coordinating abilities are both not intrinsic requirements for the growth of elongated CdSe nanocrystals.

Size Effects In The Oriented-Attachment Growth Process: The Case Of Cu Nanoseeds

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

The Size Controlled Synthesis and Self-Assembled of Monodisperse Cu2S Nanocrystals

Size Effect on Crystal Morphology of Faceted Face-Centered Cubic Fe Nanoparticles

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

Preparation of ZnO Nanoparticles with High Dispersibility Based on Oriented Attachment (OA) Process

Growth of Tin Oxide Nanorods Induced by Nanocube-Oriented Coalescence Mechanism

The Surface Condition Effect of Cu2O Flower/grass-Like Nanoarchitectures Grown on Cu Foil and Cu Film

Oriented Attachment Revisited: Does a Chemical Reaction Occur?

Controllable Synthesis of Monodisperse CuS Nanocrystals

Effect of Ligands and Growth Temperature on the Growth Kinetics and Crystal Size of Colloidal CdSe Nanocrystals

Size Refinement of Copper Nanoparticles: A Perspective from Electrochemical Nucleation and Growth Mechanism

Size disproportionation among nanocluster transformations

Nanoparticle Assembly and Oriented Attachment: Correlating Controlling Factors to the Resulting Structures

Nearly Monodisperse and Shape-Controlled CdSe Nanocrystals Via Alternative Routes: Nucleation and Growth.

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

In Situ Analysis of Growth Behaviors of Cu2O Nanocubes in Liquid Cell Transmission Electron Microscopy

Morphology-controlled Hydrothermal Synthesis and Growth Mechanism of Microcrystal Cu2O

Formation of Uniform CuO Nanorods by Spontaneous Aggregation: Selective Synthesis of CuO, Cu2O, and Cu Nanoparticles by a Solid-Liquid Phase Arc Discharge Process.