PREPARATION AND CHARACTERIZATION OF SiC POROUS CERAMICS SUPPORT
Wang Chunpeng,Su Kuifan,Deng Xiangyun,Li Jianbao,Wang Liming,Zhang Guoqing,Jing Yani,Bai Chengying
DOI: https://doi.org/10.16521/j.cnki.issn.1001-9642.2013.05.017
2013-01-01
Abstract:Using 150 μm α-SiC powder as aggregate,the mixture of kaolin,potassium feldspar and silica as binder,based on orthogonal test method,the porous ceramics support was prepared by semi dry pressing at 1350 ℃.The porosity,flexural strength,and filter pressure drop of the porous ceramics support which was made in different forming pressure,employing activated carbon and binder were investigated.The flexural strengths generally decreased with increased porosity,and the filter pressure drop enlarged along with reduced porosity.However,under the pressure of 6 MPa,the porous ceramics support was obtained with 15 wt% activated carbon and 20% binder,the flexural strength and porosity of which both raised.While under the pressure of 12 MPa,both the flexural strength and porosity of the support fabricated with 20% activated carbon and 20% binder declined.The optimization results of orthogonal test and the engineering application principle of high strength and small filtration pressure drop demonstrated that the porous ceramics support blend with 15% activated carbon and 20% binder owns 35.8% porosity,31.8 MPa flexural strength under the pressure of 12 MPa,Concomitantly,the filter pressure drop of this sample is 2.9 hPa when filtration velocity is 0.16 m·h-1.