Structure and Physical Properties of Chalcogenide Glasses

Guang Yang

2012-01-01

Abstract:This work aims at contributing to refine the structural properties of two simple glassy systems, AsₓSe₁₋ₓ and GeₓSe₁₋ₓ families. Although a lot of insightful research has been done on these glass models, their structural descriptions are still controversial. To achieve our goal, a large set of physical and structural properties was recorded on a same series of glassy samples for each family. The composition dependence of physical properties exhibit an extremum at = 2. 4 in AsxSe1-x glassy system. These results indicates a dramatic structural change at x = 0. 4, which evolves from a pyramidal network in Se-rich region and then transitions to a lower dimension structure containing an increasing number of 0-D molecular inclusions in As-rich region. Moreover, a series of physical properties throughout and above the glass transition, shows a double minimum at =2. 3 and =2. 5 with a local maximum at =2. 4. The observed trend is in agreement with the dimensionality of the network derived from structural data obtained by NMR. In binary GexSe1-x glasses, our results also indicates a dramatic structural change at x = 1/3. For the Ge-rich region, they do not support the tetrahedral model but strongly suggests that the Ge-rich glass network is closer to the GeSe crystalline phase structure. On the other hand, the viscosity of As₂Se₃ glass within the hot-zone region of the fiber drawing process was estimated using the actual temperature distribution and from standard continuum mechanics equations for a linear viscous material. Effect of ageing conditions (ageing in dark, in light and under load) on mechanical property of Te₂As₃Se₅ glass fibers has been investigated.