Abstract:Within this study, the influence of particles of different types, natures, and sizes on the mechanical and corrosion resistance of pigmented systems containing spherical zinc was studied. For this study, prominent representatives from the group of transition metal dichalcogenides (MoS2, WS2), layered transition metal oxides (MoO3, WO3), and other semiconductor materials (ZnS and ZnO) were used. The layered ultra-thin structure of these particles was predisposed to provide enhanced mechanical and anti-corrosion performance. The mechanical properties of the studied coatings were tested using standardized mechanical tests, while the anti-corrosion performance of these coatings was studied using standardized cyclic corrosion tests and the linear polarization electrochemical technique. The results of the experimental techniques bring completely original knowledge about the action of these pigments in paint systems pigmented with zinc. The results of experimental techniques have shown enhancement and an increase in both mechanical and anti-corrosion performance when using these special types of inorganic pigments. In particular, with organic coatings pigmented with MoO3, there was an increase in mechanical resistance mainly due to its morphology and layered structure. In addition, a significant enhancement of the anti-corrosion efficiency was noted for this type of organic coating due to the enhancement of individual types of action mechanisms typical and proven for zinc-pigmented systems. These original findings can be used in the search for possibilities to reduce the zinc content in zinc-pigmented organic coatings. This partial replacement of zinc particles leads not only to a reduction in the zinc content in the system but also to a significant strengthening of the mechanical resistance and an increase in the corrosion efficiency of the system.

Study on Rustproof Activity of ZnO-P_(2)O_(5)-H_(2)O Reaction System Based Zinc Phosphate Pigment

The Research Progress of Phosphate Auti-rust Pigment

Characterization and performance of organic-inorganic composite zinc phosphate with nano-sheet structure synthesized by a composite reaction of sol-gel with silane modification

Physico-chemical properties of anti-corrosion pigment based on nanoporous zeolite and zinc monophosphate

α -Zirconium hydrogenophosphate as nano-containers of 2 aminobenzimidazole for the corrosion protection of zinc in NaCl medium

Composition design and anticorrosion performance optimization of zinc molybdate pigments

Efficacy of zinc and copper oxide nanoparticles as heat and corrosion-resistant pigments in paint formulations

Hydrothermal In-Situ Synthesis and Anti-Corrosion Performance of Zinc Oxide Hydroxyapatite Nanocomposite Anti-Corrosive Pigment

Use of 2D Sulfide and Oxide Compounds as Functional Semiconducting Pigments in Protective Organic Coatings Containing Zinc Dust

Impact of inhibitor loaded with pigments content on properties of inorganic zinc rich coatings

Preparation of multifunctional waterborne rust-tolerant anti-rust coating

One Step Self-Heating Synthesis and Their Excellent Anticorrosion Performance of Zinc Phosphate/benzotriazole Composite Pigments

Anticorrosion Properties of Composite Inhibiting Pigment Based on Natural Calcium Silicate and Zinc Monophosphate

The Research Progress of Inorganic Anticorrosion Pigments

A Comparative Study on the Anti-Corrosive Performance of Zinc Phosphate in Powder Coatings

Effective Adjustment of Crystallinity and Regular Anti-Corrosion Activity of Zinc Tungstate Pigments

Mass Preparation and Anticorrosion Mechanism of Highly Triple-Effective Corrosion Inhibition Performance for Co-Modified Zinc Phosphate-Based Pigments

One-Step Preparation and Characterization of Zinc Phosphate Nanocrystals with Modified Surface

Preparation of Water-Borne Anti-Rust Coating

Preparation and characterization of Cr2O3-TiO2-Co2O3-ZnO green pigment

THE DEVELOPMENT OF ZINC-RICH PAINTS