Physico-chemical properties of anti-corrosion pigment based on nanoporous zeolite and zinc monophosphate

Sergiy Korniy,Ivan Zin,Svitlana Halaichak,Bohdan Datsko,Olha Khlopyk,Mariia Olena Danyliak,Myroslav Holovchuk

DOI: https://doi.org/10.1007/s13204-022-02592-6

2022-08-24

Applied Nanoscience

Abstract:It was studied a composite pigment based on nanoporous zeolite Na-A and zinc monophosphate synthesized by the mechanochemical method. The largest specific surface area achieved for zeolite dispersed particles is 65.3 m2/g, and their crystal structure is preserved after mechanochemical modification in a planetary mill for 60 min at 200 rpm. Mechanochemical treatment of a mixture of zeolite Na-A/Zn(H2PO4)2 initiates intercalation of phosphate in nanopores of a zeolite, which is confirmed by reducing the specific surface area of the composite pigment to 31.6 m2/g. The monophosphate modified nanoporous zeolite provides prolonged desorption of phosphate ions into a corrosion solution according to photocolorimetric results. The new composite pigment with the prolongation effect is very promising for use in anti-corrosion paints. Electrochemical studies have shown high inhibitory efficiency of zeolite Na-A/Zn(H2PO4)2 pigment suspension against corrosion of D16T aluminum alloy in 0.1% sodium chloride solution. Accordingly, the pigments can become effective inhibitory components of primer paints used for the protection of structures made of aluminum alloys under industrial environment.

nanoscience & nanotechnology