Abstract:Abstract Polymer coatings are commonly used to protect carbon steels from corrosion but they are susceptible to weathering and many of them have environmental concerns. Therefore, we studied the possibility of an environmentally favorable inorganic magnesium phosphate cement (MPC) coating for protecting mild steel. A formulation suitable for coating steel was developed by compositional modification [i.e., incremental replacement of dead-burned magnesia (MgO) with magnesium hydroxide (Mg(OH) 2 )] to a road-repair MPC. This modification yielded an acceptable working time and prevented pore formation at the coating-steel interface. Corrosion monitoring by linear polarization and electrochemical impedance spectroscopy for 14 days found that, the MPC coating substantially increased the linear polarization resistance (R p ) [e.g., day 1: (8.2 ± 1.7) × 10 3 (nadir value) vs. 495 ± 55 Ω cm −2 ] and charge transfer resistance (R ct ) (e.g., day 1: 9.3 × 10 3 vs. 3.8 × 10 2 Ω cm −2 ). The coated steel underwent neutral sodium chloride (NaCl) salt spray for 2400 h without visible rusting. Immersion for 24 h in liquids simulating the pore fluid indicated that, passivation by the excess MgO in the coating was a major contributor to its anti-corrosive property. Tafel polarization in the liquids found that, corrosion current density (I corr ) followed the rank: 3.5% NaCl solution (6.0 μA cm −2 ) > 3.5% NaCl solution containing MgO (3.6 μA cm −2 ) > 3.5% NaCl solution containing fragmented MPC (1.7 μA cm −2 ), suggesting that a physical barrier effect and dissolved phosphate ions improved its protection. This study shows that, MPC coating is a promising durable and environmentally favorable anti-corrosive material for protecting steel structures in some applications.

Corrosion Inhibition of Low-Alloy Steel by a Composite Pigment Based on Zeolite and Monocalcium Phosphate

Physico-chemical properties of anti-corrosion pigment based on nanoporous zeolite and zinc monophosphate

Anticorrosion Properties of Composite Inhibiting Pigment Based on Natural Calcium Silicate and Zinc Monophosphate

Inhibition of the Corrosion of Aluminum Alloy by a Composition of Ion-Exchange Pigments

Anticorrosive paint with a modified zeolite as functional pigment for SAE 1010 steel protection

Enhanced corrosion resistance of carbon steel in an aggressive environment by a recently developed pyrazole derivative: Electrochemical, SEM/XPS/AFM, and theoretical investigation

New Formulation of Anticorrosive Waterborne Epoxy Coatings for SAE 1010 Steel Protection

Corrosion Behavior of 304 L Steel Coated with PVB/PAn-Nano Metal Oxide (TiO2, ZnO)

Advanced Protective Films Based on Binary ZnO-NiO@polyaniline Nanocomposite for Acidic Chloride Steel Corrosion: An Integrated Study of Theoretical and Practical Investigations

Steel Corrosion Inhibition by Microbial Polysaccharide and Tartrate Mixture

Experimental and Computational Anticorrosion Behaviors of Pyrazole s-Triazine/anilino-morpholino Derivatives for Steel in Acidic Solutions

Evaluation of the Potential of Daucus crinitus Extracts and Their Synthesized ZnO Nanoparticles in Inhibiting the Corrosion of Carbon Steel

Hydrothermal In-Situ Synthesis and Anti-Corrosion Performance of Zinc Oxide Hydroxyapatite Nanocomposite Anti-Corrosive Pigment

Polyolefin-Based Smart Self-Healing Composite Coatings Modified with Calcium Carbonate and Sodium Alginate

Application of EIS and SECM Studies for Investigation of Anticorrosion Properties of Epoxy Coatings containing ZrO2 Nanoparticles on Mild Steel in 3.5% NaCl Solution

Synergistic corrosion inhibition study of Armco iron in sodium chloride by piperidin-1-yl-phosphonic acid–Zn2+ system

Enhancing steel corrosion resistance in 1.0 M HCl medium through the synthesized and characterized mixed pyrophosphates BMnP 2 O 7 (B = Ni, Co, and Cd)

Environmentally favorable magnesium phosphate anti-corrosive coating on carbon steel and protective mechanisms

Synergistically and sustainably performed inhibitors for galvanised steel against aqueous corrosion

Tailoring poly(2-ethyl-2-oxazoline) towards effective mitigation of chloride-induced dissolution of S235JR steel: The synergistic contributions of potassium iodide and myristyl trimethylammonium bromide

α -Zirconium hydrogenophosphate as nano-containers of 2 aminobenzimidazole for the corrosion protection of zinc in NaCl medium