TiC_p Interfacial Structure and Impact Wear Resistance of TiC P/ni Coating by Laser Cladding

Jun Wang

IF: 1.8

1999-01-01

Materials Science and Technology

Abstract:The TiC p interface and impact wear resistance of TiC p/Ni coating by laser cladding are studied, and compared with in situ reacted TiC p/Ni coating. It is observed that the epitaxial growth, interface reaction and precipitation appear at the TiC p interface. Under lower impact work, coatings with in situ reacted and directly-added TiC p have improved wear resistance. Under higher impact work, the wear resistance of the coating with directly-added TiC p become worse, while the wear resistance with in situ TiC p is still considerably improved. The structure character at TiC p interfaces is the major factor having effect on wear performance.