Effect of TiC content on microstructure and properties of TiC/Ni60 coatings on Ti6Al4V alloy deposited by laser cladding

Qun Cai,Gang Li,Biao Wu,Shengyu Xu,Lyuyuan Wang,Yupeng Guo
DOI: https://doi.org/10.1016/j.optlastec.2023.109854
IF: 4.939
2024-01-01
Optics & Laser Technology
Abstract:In this study, the composite coatings on Ti6Al4V alloy are fabricated with TiC and Ni60 mixture powders by laser cladding. The effect of TiC content on microstructure and properties of the coatings is investigated. Many TiC particles in large size are randomly distributed in the coatings. The coatings mainly contain TiC. TiC, TiC x , Ti2Ni, TiNi, TiB, Cr x B and Ti phase identified by XRD. The feature of the precipitates in the coatings is various due to different TiC. The forms of the precipitates are changed in the coatings with increasing the TiC content. The wear resistance of the coatings decreases with increasing the TiC content. Numerous plowing grooves with the debris particles and white scaly patterns are found in the sliding direction. With increasing the TiC content, the bending strength of the samples decreases. The brittle fracture feature are shown on the fracture surface of the coatings.
optics,physics, applied
What problem does this paper attempt to address?
The paper mainly explores the effect of TiC (titanium carbide) content on the microstructure and properties of TiC/Ni60 composite coatings formed by laser cladding on Ti6Al4V alloy. Specifically, the study prepared composite coatings with different TiC contents using laser cladding technology and investigated how changes in TiC content affect the microstructure and properties of these coatings. The substrate material used in the experiment was a 2 mm thick Ti6Al4V alloy plate, and the powder materials included TiC powder with a particle size of 50-100 microns and Ni60 powder. The coatings were obtained by laser cladding treatment after mixing these two powders in different proportions. The study found that with the increase in TiC content, the number of TiC particles in the coating increased, leading to changes in the microstructure of the coating. Various phases appeared in the coating, such as TiC, TiCx, Ti2Ni, TiNi, TiB, CrxB, and Ti phases. In addition, the hardness of the coating increased with the increase in TiC content, but the wear resistance decreased. Wear tests showed that a large number of plow marks and white flake-like patterns appeared on the coating surface. Furthermore, with the increase in TiC content, the bending strength of the coating also decreased, and the fracture surface exhibited obvious brittle fracture characteristics. In summary, this study aims to explore the specific impact of TiC content on the performance of TiC/Ni60 composite coatings, which is of great significance for optimizing the application of such coatings.