Microstructure and Properties of AZ91D Magnesium Alloy by Solid-State Recycling

Zesheng Ji,Yang Xu-yue
2006-01-01
Abstract:AZ91D magnesium alloy was prepared by hot extrusion of machined chips at 573,623,673 and 723K with an extrusion ratio of 11∶1,subsequently its microstructure and mechanical properties were investigated.The results indicate that the ultimate tensile strength and elongation of AZ91D magnesium alloys increase with the elevation of preparation temperature at 573673K,and decrease with the elevation of preparation temperature above 673K,and its ultimate tensile strength is the best at 673K and can reach 384.4MPa.Compared with the as-cast specimens and the extruded specimens from cast ingot,the mechanical properties of the AZ91D magnesium alloy improve evidently because the oxide layers are dispersed in the structure and the dynamic recrystallization happens in the extrusion process.When the preparation temperature is 673K,the elongation is 5.8%,and it is 152% higher than that of the as-cast specimens.The AZ91D magnesium alloy machined chips can't be connected completely and a lot of cracks appear during the extrusion process.Compared with the extruded specimens from cast ingot at 673K,the elongation is 44% lower.
What problem does this paper attempt to address?