Study on the Self-hardened Phosphate Sand

Meng Li

2002-01-01

Abstract:The optimum composition of the selfhardened phosphate sand has been determined through the orthogonal experiments utilizing the acid phosphate as cohering agent and the alkaline slag as solidifying accelerant.The product features\+′ tests and the small quantity productoin show that this product is of great economic significance.

What problem does this paper attempt to address?

Study on Properties of Microwave Hardened Inorganic Phosphate Binder Foundry Sand

Dong LIU,Youshou ZHANG,Lu XIA,Jin HUANG

DOI: https://doi.org/10.16410/j.issn1000-8365.2018.01.007

2018-01-01

Abstract:Foundry industry urgently called for a more environmental friendly foundry binder.Properties of a phosphate binder and its microwave hardened sand was studied.Effects of binder chemical,electric power and heating time on sand strength,moisture resistance and sand knockout were researched.The results show that matters such as organic acid,inorganic acid and harmless polymer modified phosphate binder sand has long work time,high dry strength,tensile strength being 2 MPa.Moisture resistance is improved by a compound oxide.Sand knockout matches organic sand.The sand can be used to take the place of resin coated sand and has exceptional environmental superiority.
Study and Application on No Bake Phosphate High Chromite-Corundum Sand

HUANG Jin,ZHANG You-shou,XIA Lu,LI Si-nian,HUANG Nai-yu

DOI: https://doi.org/10.3321/j.issn:1001-4977.2006.07.015

2006-01-01

Abstract:A high neutralization degree compounded aluminum phosphate binder is synthesized. No bake phosphate mixture, composed of the binder, high chromite corundum sand and fused magnesia powder, has good room temperature and high temperature strength, moderate retained strength and low hydroscopicity. A difficult foundry problem about the cast shaping of the small and deep holes in the heavy section steel castings can be solved by using the no bake sand for making cores.
Study of Environmentally Friendly Phosphate-Bonded No-Bake Sand

Dan He,Lu Xia,Jin Huang,Youshou Zhang

DOI: https://doi.org/10.4028/www.scientific.net/amr.602-604.1161

2013-01-01

Abstract:Regarding dry strength as the index, and considering liftability and storage stability, effects of solidification agent amount and organics N on the property of high neutralization degree phosphate no-bake sand mold/core were studied by modifying the binder coded 32B8M15 and adding solidification agent fused MgO in sand mixing. A new type of compound phosphate binder coded 32B8M15N4 is developed, and results indicate that, at environment condition of below 15°C and 50% RH, the proper solidification agent amount is 5% when using high neutralization degree binder coded 32B8M15N4 (its addition amount is 3%) to make no-bake sand, its molding sand sample has high dry strength and good storage stability, its compressive strength, σ0, σ1, σ2, σ3, σ4 is 2.33 MPa, 2.27 MPa, 2.01 MPa, 2.03 MPa, 2 MPa separately.
Optimizing Study of Solidification Agent with High Neutralization Degree Compound Phosphate-Bonded No-Bake Sand by Orthogonal Test

Dan He,Lu Xia,You Shou Zhang,Jin Huang

DOI: https://doi.org/10.4028/www.scientific.net/amr.721.337

2013-01-01

Advanced Materials Research

Abstract:Regarding dry strength and storage strength of high neutralization degree compound phosphate no-bake sand as index, optimization was analyzed on the ratios of solidification agent to obtain the appropriate adding amount in different environment by orthogonal test, and influence of optimum formula on the storage stability of the no-bake sand was studied. The results show that, in condition of up 25°C, when humidity is more than 60% RH, the formula of solidification agent is 5% Mg-contained powder + 2% Al-contained powder + 4% Zn-contained powder, its no-bake sand sample has high dry strength and good storage stability. When humidity is less than 60% RH, the formula of solidification agent is 2% Mg-contained powder + 2% Al-contained powder + 4% Zn-contained powder, its no-bake sand sample has high dry strength and good storage stability.
Study on the Storage Stability of High Neutralization Degree Phosphate-Bonded No-Bake Sand

Lu Xia,Wei Long,You Shou Zhang,Jin Huang,Bu Song Hu

DOI: https://doi.org/10.4028/www.scientific.net/amr.941-944.981

2014-01-01

Advanced Materials Research

Abstract:Effect of particle size of Al (OH)3 and Mg-containing modifier of binder and hardener on the dry strength and storage stability of high neutralization degree phosphate-bonded no-bake sand were studied. Results show that particle size of Al (OH)3 has little effect on the dry strength and storage stability when its varieties are 4.552 μ m toothpaste-grade Al (OH)3 and 6.136μm industrial special Al (OH)3, 6.136μm industrial special Al (OH)3 is more appropriate in consideration of cost and source. Adding Mg-containing modifier to binder code 32B8M15B cannot improve the dry strength and storage stability, but adopting compound modifier, 2% fused magnesia powder+2% iron powder+4% copper powder ,can obtain better properties , dry strength can reach 3.022MPa, and the minimum strength is above 1MPa with humidity fluctuation from 21%RH to 60%RH in 18 days.
Study on Properties of Phosphate Binder No-Bake Sand

Zhang Youshou,Hu Fanjian,Huang Jin,Xia Lu

DOI: https://doi.org/10.3969/j.issn.1000-6826.2007.06.018

2007-01-01

Abstract:The properties of phosphate binder of no bake sand such as sand mixing technique,the amount of binder and hardener,the scrip time and work time,the shakeout property and humidity resistance are studied in the paper.The experiment showed that the phosphate binder has general technique property and can satisfy practical use.
Study on the Iron Oxide Composite Hardener in Phosphate No-bake Sand

HU Tu,ZHANG You-Shou,XIA Lu,HUANG Jin

DOI: https://doi.org/10.3969/j.issn.1674-6694.2011.04.016

2011-01-01

Abstract:By adding iron oxide to the unitary magnesium oxide,a composite harder is prepared.The results showed that the composite harder can increase the tensile strength of phosphate no-bake sand more than 60%,the store stability of phosphate no-bake sand was also improved.Changing the percentage of the iron oxide,it showed that the addition quantity of iron oxide and the property of sand was nonlinearity.The highest tensile strength was obtained by 20% content of iron oxide based on total composite hardener.But a higher sand store stability was attained by 30% iron oxide.Putting this no-bake sand under high humidity(more than 90%RH)condition for 24 hours,the no-bake sand become flexible and the tensile strength is decreased.
A New Phosphate Binder for Making Sand Mold or Core for Aluminum Alloy Castings

Youshou Zhang,Yiyu Xue,Jin Huang,Lu XIA,Caihua Huang

DOI: https://doi.org/10.3321/j.issn:1001-2249.2005.08.018

2005-01-01

Abstract:A new binder for making sand mold or core suitable for low melting point metal or alloy, such as aluminum alloy, and its hardening process were investigated. The sand mold or core with good collapsibility can be obtained due to having higher strength in surface layer and lower strength in hearted part, which is benefit for cleaning sand on components. The binder exhibits good collapsibility and pollution free behavior compared with organic binder.
Research on New Al-Mg-B Compound Phosphate Inorganic Binder for Heat Cured Sand

XIA Lu,HUANG Jin,ZHANG Youshou

DOI: https://doi.org/10.3969/j.issn.1001-3814.2008.17.003

2008-01-01

Abstract:The aluminum phosphate foundry inorganic binder for heat cured sand was compounded and modified by joining different inorganic substance. The results show that a kind of Al-Mg-B compound phosphate inorganic binder has good comprehensive properties, its stability can reach 10 months, its heat cured sand mould and core has good collapsibility, higher dry strength and good humidity resistance in flowing air and high humidity.
Mechanism of Strength Loss of No-Bake Phosphate Bonded Sand Mold/core

Youshou Zhang,Yiyu Xue,Jin Huang,Sinian Li,Lu Xia,Caihua Huang

DOI: https://doi.org/10.1007/s11595-009-1005-z

2009-01-01

Journal of Wuhan University of Technology-Mater Sci Ed

Abstract:The strength loss mechanism of the phosphate bonded sand mold/core was studied. The morphology and composition of phosphate membrane on the surface of sands was analyzed with electron probe X-ray microanalyzer. Results show that magnesium causes cracks in cured phosphate membrane and results in the decrease of sand molds/cores strength. However, the addition of magnesium significantly enhanced hygroscopy resistance of phosphate membrane. In addition, the phosphate binder added with the magnesium modifier has more rapid hardening reaction speed compared that without or with low magnesium binder. It can be concluded that the phosphate binder with the addition of magnesium modifier is favorably used in high humid and cold circumstance.
Discuss of Bond Mechanism of AI-phosphate Hot Cured Sand

XIA Lu,ZHANG You-shou,HUANG Jin,DONG Shi-jie,LI Si-nian

2011-01-01

Abstract:Based on the dry strength testing of Al-phosphate hot cured sand samples,the bond mechanism was discussed,and the effect of modifier on bond mechanism was analyzed by SEM and EMPA.It is revealed that fracture mode of Al-phosphate hot cured sand sample is basically adhesive fracture and brittle fracture with low dry strength and small among of binding points between sand particles.Fracture mode of Al-phosphate hot cured sand is changed from adhesive fracture and brittle fracture to cohesive fracture and plastic fracture and the binding bridge are refined and amount of cracks in binding bridge are reduced after adding magnesium containing modifier and boron containing modifier simultaneously.Viscosity of binder is improved at the same density after adding magnesium-containing modifier,and binding points between sand particles are increased,so that the dry strength is improved too.
A Study on the Modified Aluminosilicate Sand Stabilization Material

李婷,邓湘云,李建保,陈永,张海涛,章文

2010-01-01

Abstract:Advanced perf ormance sand stabilization material is prepared by method of chemical sand fixation, using water glass and aluminium chloride as agglomerant and curing agent,respectively.The structure and constituent of the adhesive are characterized by X-ray diffraction and infared spectroscopy,and a probable explanation of formation mechanism is analyzed for the high performance of sand stabilization material.It is concluded that the amorphous poly-aluminosilicate containing Si-O-Al bonds which is synthesized by reaction between Si(OH)_4 and AlCl_3 play an important role in improving mechanical properties of the sand stabilization material.
Study on Properties of Phosphate Inorganic Resin and No-Bake Mold or Core

XIA Lu,ZHANG You-shou,HUANG Jin

DOI: https://doi.org/10.3969/j.issn.1674-6694.2006.02.006

2006-01-01

Abstract:The characteristics of no bake sand mold or core with phosphate binder system were studied in this paper.The mixing technique,amount of binder,amount of hardener,strip time,work time and shakeout property have been studied.The experiment showed that the phosphate binder has good comprehensive property and can satisfy practical use.
Study on B-Al-Mg Compound Phosphate Binder by Orthogonal Test Method

XIA Lou,ZHANG You-shou,HUANG Jin,LI Si-nian,XUE Yi-yu

DOI: https://doi.org/10.3969/j.issn.1000-8365.2006.02.005

2006-01-01

Abstract:The superior formula of B-Al-Mg compound phosphate foundry binder has been studied by applying orthogonal experiment. The target of orthogonal experiment is to get high room temperature compressive strength of core or sand mold. Considering another performance, the anti-moisture absorption, the final formula was obtained by improving the superior formula. Tests show that the no-bake sand bonded by this kind of compound phosphate binder has high room temperature compressive strength and good anti-moisture absorption.
Experimental study on strength and abrasion-resistance enhancement admixture

DeJin Xu,ChuanQing Fu,Xianyu Jin,Tian Ye,Jin Guo Jin

DOI: https://doi.org/10.4028/www.scientific.net/AMR.250-253.247

2011-01-01

Abstract:Cement concrete has an increasing utilization in highway construction. However, the lower flexural tensile strength and abrasion-resistance restricted the development of concrete pavement with heavy traffic. Hence, It has highlighted the need for research on high performance concrete (HPC). The design of specific concrete normally depends on the mixing of mineral admixtures in concrete mixture. This paper presents the first experimental study on strength and abrasion-resistance enhancement admixture (SAEA) mixed with slag powder, steel slag powder and silica fume. The optimal proportion of three mineral admixture and reasonable mixed amount of SAEA were then given, and the mechanism of SAEA reacted in concrete was analyzed based on sol-gel theory. Lastly, the effect of concrete mixed with SAEA was validated and the micro-structure transformation of specimens was given by SEM.
Investigation of the Relationship among the Hydration, Microstructure and Compressive Strength of Alkali-Activated Phosphorus Slag

Ruiquan Jia,Qiang Wang,Ting Luo

DOI: https://doi.org/10.1016/j.jobe.2023.107293

IF: 7.144

2023-01-01

Journal of Building Engineering

Abstract:In this study, the relationship among the hydration, microstructure and compressive strength of alkali-activated phosphorus slag (AAPS) was systematically investigated to provide a foundation for its design and application. The alkali dose and silicate modulus had both positive and negative effects on PS hydration due to the change in the pH, the concentrations of Si-containing ions and the hydrate coating on the PS surface, and the overall effect depended on their relative magnitudes. The hydration of waterglass-activated phosphorus slag (WAPS) experienced a transformation of NASH first into CNASH (low Ca) and then into CNASH (high Ca) due to the stronger polarization ability of Ca2+ over Na+, and the gel transformation was accompanied by dealumination. The more early hydrates there were, the higher the early densification and early compressive strength of AAPS. The later densification and later compressive strength were influenced by a combination of the hydrate content, early hydration rate and gel type. CNASH (high Na) was incompatible with CNASH (low Na), which degraded the later densification. When the contents of later hydrates were comparable, the slower early hydration and lower CNASH (high Na) contributed to the greater later densification and compressive strength.
Study on the Humidity Resistance of the No-bake Al-phosphate Sand

XIA Lu,ZHANG You-shou,HUANG Jin

DOI: https://doi.org/10.3969/j.issn.1003-4684.2006.03.027

2006-01-01

Abstract:The humidity resistance of the no-bake Al-phosphate sand was improved with the addition of the modifier to the no-bake Al-phosphate binder and changing the solidification humidity.The test result has been analyzed by means of EPMA in this paper.It is revealed that the humidity resistance of the no-bake Al-phosphate sand is improved by the suitable modifier.The effect is more remarkable when the no-bake phosphate sand is solidified under the high humidity,and the humidity resistance of the no-bake Al-phosphate sand is improved when the amount of MgHPO_4·XH 2O in the gelatin product is appropriate.
Exploration on the Composite Hardener for No-Bake Phosphate Binder Sand

商宏飞,张友寿,夏露,黄晋

2010-01-01

Abstract:Some composite hardeners were prepared which content some other substances besides magnesia,and comparison was made with traditional magnesia hardener.The results show that there are two composite hardeners are better among the tested composite hardeners,one is composed of magnesia and 20% iron,the other one is composed of magnesia and 30% copper oxide.It is proved by pouring experiments with satisfactory.
Parametric optimization of modifiers for ester-hardened sodium silicate bonded sand

Guoli Song,Xueshan Du,Ming Zhang,Yufu Sun,Nan Cheng

DOI: https://doi.org/10.1080/10426914.2020.1718697

IF: 4.7832

2020-01-21

Materials and Manufacturing Processes

Abstract:In this paper, the parameters of composite modifiers composed of polyvinylpyrrolidone (PVP), lithium tetraborate and disodium hydrogen phosphate for ester-hardened sodium silicate bonded sand (SSBS) were optimized by orthogonal experiment. The results of orthogonal experiment showed the optimal parameters of PVP, lithium tetraborate and disodium hydrogen phosphate were 8%, 0.15% and 0.2% of sodium silicate binder, and the1 h tensile strength (σ1 h) and the 24 tensile strength (σ24 h) of modified sand samples increased by 44% and 66% and the residual strength (σ950°C) decreased by 49%. The experimental results indicated that the modifiers promoted the bonding bridges of sand sample smoother and tighter at room temperature, which improved the 1 h and 24 tensile strength, and facilitated the formation of Na2Si2O5, Na3PO4, Na4B2O5 and Li2B8O13 and the volatilization of PVP in the process of heating and cooling at 950°C, resulting in the formation of cracks and blow holes on bonding bridges, thereby improving the collapsibility of SSBS.

materials science, multidisciplinary,engineering, manufacturing
Study on Phosphate Foundry Binder Modified by Citric Acid

杨金,张友寿,夏露,黄晋,李四年

DOI: https://doi.org/10.3969/j.issn.1674-6694.2008.05.012

2008-01-01

Abstract:The modification of phosphate binder by citric acid was stuided in this paper.Experiments showed that good stability of high neutralization degree phosphate binder was obtained modified by citric acid,but stability of low neutralization degree phosphate binder was damaged by citric acid.Strength of no-bake sand was raised to some extent by citric acid,especially in rapid reaction.Air humidity has great effect on strength of citric acid modified binder sand.

Study on the Self-hardened Phosphate Sand

Study on Properties of Microwave Hardened Inorganic Phosphate Binder Foundry Sand

Study and Application on No Bake Phosphate High Chromite-Corundum Sand

Study of Environmentally Friendly Phosphate-Bonded No-Bake Sand

Optimizing Study of Solidification Agent with High Neutralization Degree Compound Phosphate-Bonded No-Bake Sand by Orthogonal Test

Study on the Storage Stability of High Neutralization Degree Phosphate-Bonded No-Bake Sand

Study on Properties of Phosphate Binder No-Bake Sand

Study on the Iron Oxide Composite Hardener in Phosphate No-bake Sand

A New Phosphate Binder for Making Sand Mold or Core for Aluminum Alloy Castings

Research on New Al-Mg-B Compound Phosphate Inorganic Binder for Heat Cured Sand

Mechanism of Strength Loss of No-Bake Phosphate Bonded Sand Mold/core

Discuss of Bond Mechanism of AI-phosphate Hot Cured Sand

A Study on the Modified Aluminosilicate Sand Stabilization Material

Study on Properties of Phosphate Inorganic Resin and No-Bake Mold or Core

Study on B-Al-Mg Compound Phosphate Binder by Orthogonal Test Method

Experimental study on strength and abrasion-resistance enhancement admixture

Investigation of the Relationship among the Hydration, Microstructure and Compressive Strength of Alkali-Activated Phosphorus Slag

Study on the Humidity Resistance of the No-bake Al-phosphate Sand

Exploration on the Composite Hardener for No-Bake Phosphate Binder Sand

Parametric optimization of modifiers for ester-hardened sodium silicate bonded sand

Study on Phosphate Foundry Binder Modified by Citric Acid