Abstract:Composite briquettes containing high-phosphorus oolitic hematite and coal were produced with a twin-roller briquette machine using sodium carboxymethyl cellulose,molasses,starch,sodium silicate,and bentonite as binders.The effect of these binders on the strength of the composite briquettes,including cold strength and high-temperature strength,was investigated by drop testing and compression testing.It was found the addition of Ca（OH）2 and Na2CO3 not only improved the reduction of iron oxides and promoted dephosphorization during the reduction-separation process but also provided strength to the composite briquettes during the briquetting process; a compressive strength of 152.8 N per briquette was obtained when no binders were used.On this basis,the addition of molasses,sodium silicate,starch,and bentonite improved the cold strength of the composite briquettes,and a maximum compressive strength of 404.6 N per briquette was obtained by using starch.When subjected to a thermal treatment at 1200°C,all of the composite briquettes suffered from a sharp decrease in compressive strength during the initial reduction process.This decrease in strength was related to an increase in porosity of the composite briquettes.X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses showed that the decrease in strength of the composite briquettes could be caused by four factors: decomposition of bonding materials,gasification of coal,transportation of byproduct gases in the composite briquettes,and thermal stress.

Study on the Iron Oxide Composite Hardener in Phosphate No-bake Sand

Exploration on the Composite Hardener for No-Bake Phosphate Binder Sand

Study on the Storage Stability of High Neutralization Degree Phosphate-Bonded No-Bake Sand

Study on the Humidity Resistance of the No-bake Al-phosphate Sand

Study and Application on No Bake Phosphate High Chromite-Corundum Sand

Effect of Factors on Strength and Stability in No Bake Sand Phosphate Inorganic Binder

Study of Environmentally Friendly Phosphate-Bonded No-Bake Sand

Optimizing Study of Solidification Agent with High Neutralization Degree Compound Phosphate-Bonded No-Bake Sand by Orthogonal Test

Study on Properties of Phosphate Binder No-Bake Sand

Effect of Modifiers on Properties of No-bake Aluminium Phosphate Sand

Study on Properties of Microwave Hardened Inorganic Phosphate Binder Foundry Sand

Study on Properties of Phosphate Inorganic Resin and No-Bake Mold or Core

Study on the Self-hardened Phosphate Sand

Research on New Al-Mg-B Compound Phosphate Inorganic Binder for Heat Cured Sand

Mechanism of Strength Loss of No-Bake Phosphate Bonded Sand Mold/core

Preparation and Characterization of Magnetite-Based Iron Phosphate Cement

Study on the Strength of Cold-Bonded High-Phosphorus Oolitic Hematite-Coal Composite Briquettes

Study on B-Al-Mg Compound Phosphate Binder by Orthogonal Test Method

Magnesia Hardener for Phosphate Binder

Effect of Boron-contaning Modifier on the Properties of Heat-cured Aluminum Phosphate Inorganic Binder-bonded Sand

Study on Phosphate Foundry Binder Modified by Citric Acid