High-performance Supercapacitor Materials Based on Polypyrrole Composites Embedded with Core-Sheath Polypyrrole@mnmoo4 Nanorods

Huan Wang,Yahui Song,Jingkuo Zhou,Xiaoyang Xu,Wei Hong,Jing Yan,Ruinan Xue,Huilin Zhao,Yu Liu,Jianping Gao

DOI: https://doi.org/10.1016/j.electacta.2016.07.035

IF: 6.6

2016-01-01

Electrochimica Acta

Abstract:In this study, a binary composite [email protected]4 was facilely prepared via in situ oxidative polymerization of monomer in the presence of MnMoO4 nanorods The MnMoO4 nanorods were wrapped by a layer of polypyrrole (PPy) and formed a core-sheath structure which embedded in PPy matrix. The prepared [email protected]4 composite was characterized by XRD, IR, SEM, and TEM spectroscopy and its capacitive performance was investigated. Electrochemical measurements show that the specific capacitance of [email protected]4 composite (MnMoO4 content is 13.95 wt%) reached 462.9 F g−1 at a scan rate of 5 mV s−1 and 374.8 F g−1 at a current density of 0.2 A g−1 in a three-electrode system. In the two-electrode system of a symmetric supercapacitor, it achieved specific capacitances of about 221.3 F g−1 at a scan rate of 5 mV s−1 and 207.5 F g−1 at a current density of 0.5 A g−1. The [email protected]4 retained 80.6% of its initial capacitance after 1000 cycles. The excellent electrochemical performance of [email protected]4 composite is attributed to the synergistic effects between the polymer chain and MnMoO4 in [email protected]4 and its well-designed structure.