Abstract:Electrochemical electric double layer capacitors (EDLC) known as supercapacitors are used for high power density, long cycle life and good reversibility of charge/discharge processes[1]. Recent years, many Schiff base transition metal composites acting as an electroactive electrode material deposited on carbon nanotubes(CNTs) have been researched[2]. However, the CNTs tend to be random orientation, twining round and cross linked. So it urgently need to be addressed. In this paper, a given mass of NH4BF4 was added to CNTs and the electrode was prepared by the homodispersion of the raw support material in N-methyl- 2-pyrrolidone (NMP) through sonicating. The slurry was coated on a Ti sheet with the coating mass of 0.3 mg. The electropolymerization of Ni(salen) on the resulting electrode was conducted in a closed three-electrode compartment cell adopted chronoamperometry method. The introduction of NH4BF4 to the CNTs with a specific percentage (5wt. %, 10wt. %, 15 wt. %), and the modified samples were named as NBF5, NBF10, NBF15 respectively and the CNTs without NH4BF4 were taken as a control group and named as NBF0. As the cyclic voltammetric data summarized in Table 1, the values of apparent surface coverage(Γ) and doping level(n) of NBF5, NBF10 and NBF15 didn't appear to be much different from those of NBF0. However, the specific capacitance varied a lot. It can be seen that Cm of NBF15 is the most among the samples. Figure 1 depicts the GCD plots of the composite and CNTs at the current density of 1.0 mA cm-2. CNTs have symmetric change in the charge/discharge process which is the characteristic of high Coulombic efficiency. It is clear that the composites possess longer charge/discharge time than CNTs which indicating that poly[Ni(salen)] contributes the pseudo-capacitance derived from reversible redox switching between neutral and oxidative states on the basis of electric double-layer capacitance of MWCNTs. Because of the introduction of NBF, it became difficult for CNTs to twint together disorderly. And the morphylogy of the electrode support got homogeneous. NBF-containing carbon nanotube could provide basic sites, and consequently improved the deposition of polymer and enhance the performance of the electrode material. Acknowledgement This work is financially supported by the National Natural Science Foundation of China (No. 51372021). References [1] D. Kaufman, K.L. Hudson, R. Mcclamrock. Science. 343 (2014) 1210–1211. [2] Y. Zhang, J. Li, F. Gao, F. Kang, X. Wang, F. Ye, J. Yang. Electrochim. Acta. 76 (2012) 1–7. Figure 1

Fabrication of Carbon Nanotubes/Polypyrrole/Carbon Nanotubes/Melamine Foam for Supercapacitor

Core-shell structured carbon nanofibers yarn@polypyrrole@graphene for high performance all-solid-state fiber supercapacitors

The Enhanced Capacitance Performance of the Modified Polypyrrole with the Mixture of Carbon Nanomaterials

Multiwalled Carbon Nanotubes/Polypyrrole/Graphene/Nonwoven Fabric Composites Used As Electrodes of Electrochemical Capacitor

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Preparation of a Three-Dimensional Ordered Macroporous Carbon Nanotube/Polypyrrole Composite for Supercapacitors and Diffusion Modeling

Flexible Electrodes Based on Polypyrrole/manganese Dioxide/polypropylene Fibrous Membrane Composite for Supercapacitor

The Electrochemical Performance of Nitrogen-Containing Carbon Nanotubes As the Electrode Material of Supercapacitors

In-situ synthesis of carbon nanotube/graphene composite sponge and its application as compressible supercapacitor electrode

Synthesis of Metal Oxide Decorated Polycarboxyphenyl Polymer-Grafted Multiwalled Carbon Nanotube Composites by a Chemical Grafting Approach for Supercapacitor Application

Nitrogen, Boron and Fluorine Tri-Doped Carbon Nanotubes on Carbon Cloth As the Electrode Materials for Supercapacitors

Synthesis of polypyrrole/nitrogen-doped porous carbon matrix composite as the electrode material for supercapacitors

Defective Super-Long Carbon Nanotubes and Polypyrrole Composite for High-Performance Supercapacitor Electrodes

Carboxylated multi-walled carbon nanotube/polyaniline composites for high-performance supercapacitor electrodes

Mesoporous carbon nanofiber engineered for improved supercapacitor performance

Carbon Nanotube-Polypyrrole Core-Shell Sponge and Its Application As Highly Compressible Supercapacitor Electrode

Design of NiCo 2 O 4 nanoparticles in-situ grown on lignin-derived porous carbon and MWCNTS composites for supercapacitors

Polyimide‐based Porous Hollow Carbon Nanofibers for Supercapacitor Electrode

Nacre-Like Laminate Nitrogen-Doped Porous Carbon/Carbon Nanotubes/Graphene Composite For Excellent Comprehensive Performance Supercapacitors

Synthesis And Characterization Of A Novel Tube-In-Tube Nanostructured Ppy/Mno2/Cnts Composite For Supercapacitor

Structural evolution of carbon foam and its effect on polypyrrole/carbon foam composite electrodes in supercapacitors