Abstract:This research has demonstrated that SiO 2 impregnation under high vacuum pressure of − 90 kPa can significantly reduce porosity by almost 10%, and improve the mechanical and viscoelastic properties of spruce wood under dry and saturated states. Characterization methods, such as impact test, DMA, SEM, EDS, porosity and SAXS tests were conducted on non-treated and − 90 kPa treated spruce wood samples under dry, saturated and submerged states to analyze the synergistic effect of high vacuum SiO 2 impregnation pressure on wood properties. The results showed that high vacuum impregnation pressure had a significant positive reinforcing effect on wood's properties. It increased the impact resistance of wood under dry and saturated conditions. Additionally, the high vacuum impregnation technique was able to overcome the water-induced softening effect and caused a significant increase in the storage modulus through uniform dispersion of the SiO 2 particles in the wood's vascular structure. Consequently, the impregnation reinforced the wood and ameliorated its capacity to absorb energy. High vacuum impregnation was also able to counteract the plasticizing effect of the water molecules and significantly increased the loss modulus by increasing the internal friction and cohesion of the wood components with the addition of the nanoparticles to the vascular system, which increased the wood's capacity to transform and dissipate energy. Quantitatively and qualitatively, impregnation under a vacuum pressure of − 90 kPa exhibited an effective obstruction of the vascular structure of spruce wood. In all conditions, high vacuum-impregnated samples showed significant enhancements over non-treated samples. This research demonstrated that high vacuum SiO 2 impregnation is an effective wood processing technique. Multiple materials and applications could benefit from this research wherein high strain-rate deformations are expected to occur or when simultaneous elastic behaviour of wood and its damping energy is needed. This study could also pave the way for research on the synergistic effect of SiO 2 impregnation and water absorption on the viscoelastic behaviour of wood.

The Effect of Microwave Pretreatment on the Impregnation of Poplar Wood

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Effects of different incising pretreatments in improving permeability in two refractory wood species

Effect of microwave treatment on the wood structure of Norway spruce and radiata pine

The study of physico-mechanical properties of SiO2-impregnated wood under dry and saturated conditions

Improving gas permeability and characterizing the multi-scale pore size distribution of radiata pine (Pinus radiata D. Don) treated via high-intensity microwave

Decay resistance and mechanical strength of poplar wood treated after injection treatment to living trees using ammoniacal copper quaternary/carbon dots

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

EFFECT OF MODIFICATION WITH MELAMINE–UREA–FORMALDEHYDE RESIN ON THE PROPERTIES OF EUCALYPTUS AND POPLAR

Dyeing of Poplar Wood Through High-Pressure Processing: Performance Evaluation

Preparation Optimization of Enhanced Poplar Wood by Organic–Inorganic Hybrid Treatment via Response Surface Methodology

Effects of High-Temperature Heat Treatment Modification by Impregnation on Physical and Mechanical Properties of Poplar

Effect of Pretreatment on Permeability of Aspen Wood Veneers

Research on the Impregnation Process and Mechanism of Silica Sol/Phenolic Resin Modified Poplar Wood

Effect of microwave pre-treatment on preservative retention and treatability of Melia composita wood

Permeability of wood impregnated with polyethylene wax emulsion in vacuum

The Pit Membrane Changes of Micro-Explosion-pretreated Poplar

EFFECTS OF MOISTURE ON DRYING RATE OF MICRO- EXPLOSION-PRETREATED FAST-GROWING POPLAR WOOD

Effect of Phenol Formaldehyde Resin Penetration on the Quasi-Static and Dynamic Mechanics of Wood Cell Walls Using Nanoindentation

Preparation of highly-densified modified poplar wood by evacuating the micro-pores of wood through a gas expansion method

Manufacturing and Characterization of Modified Wood with In Situ Polymerization and Cross-linking of Water-Soluble Monomers on Wood Cell Walls