Abstract:[Objective] The aim of this study is to explore the influence of different post-treatment and drying methods on weight percent gain (WPG) and dimensional stability of the melamine-urea-formaldehyde (MUF) resin impregnated wood,to provide reference to modification technique with resin-impregnation.[Method] The MUF resin solutions with concentrations of 5％,10％,15％,25％ were used to impregnate poplar wood (Populus tomentosa) using the full cell treatment schedule.After the impregnation,specimens were treated respectively under 4 conditions:air drying for seven days,storing in high humidity condition for seven days,soaked in the resin solution for seven days,and no posttreatment.Subsequently,the post-treated specimens were sorted into two groups and took direct drying and wet drying respectively,followed by the measurements of the WPG and bulking.Finally,resin treated specimens and untreated specimens were immersed in distilled water for fourteen days.Once the specimens were taken out from the distilled water,the anti-swelling efficiency and the ratio of radial swelling to tangential swelling were determined.[Result] It was found that there was a significant positive correlation between WPG and resin content.The WPG of specimens impregnated with resin content of 5％,10％,15％,and 25％ was 9.7％,19.1％,28.4％,and 50.0％ respectively,and no obvious differences in WPG was observed between specimens with different post-treatments.After the same post-treatment,specimens through direct drying had a slightly lower WPG than those through wet drying.Specimens stored in a high humidity condition or soaked in the resin solution after resin impregnation had a higher bulking ratio than those through other post-treatments.Wet drying resulted in a higher bulking ratio than direct drying after the same post-treatment except for the air drying.The changes in anti-swelling efficiency for resin impregnated specimens under different post-treatments corresponded to those in bulking ratio.The radial and tangential swelling of the resin impregnated wood decreased with the increase in WPG,while the ratio of radial swelling to tangential swelling also increased.The ratio of radial swelling to tangential swelling of the resin impregnated specimens at low WPG was smaller than that of the untreated wood,but larger than that of the untreated wood with WPG above about 30％.[Conclusion] 1) Post-treatment has less influence on WPG than the drying process.The wet drying process is conducive to resin fixation in wood pores,resulting in a higher WPG.2) Cell wall bulking ratio is influenced by the post-treatment method as well as the drying process.Storing the specimens in high humidity condition or soaking them into the resin solution after the resin impregnation would result in more resin penetrating into the cell wall.Wet drying process would favor more resin penetrating through and fixing at cell walls,and therefore,result in higher bulking ratio.3) Anti-swelling efficiency correlates with cell wall bulking ratio of the resin impregnated specimens,and the higher bulking ratio would results in higher anti-swelling efficiency and better dimensional stability.4) The ratio of radial swelling to tangential swelling increases with the increase in WPG.

EFFECT OF MODIFICATION WITH MELAMINE–UREA–FORMALDEHYDE RESIN ON THE PROPERTIES OF EUCALYPTUS AND POPLAR

EFFECTS OF MODIFICATION WITH MELAMINE–UREA–FORMALDEHYDE RESIN ON THE PROPERTIES OF UREA PRETREATED EUCALYPTUS

Effect of Low Molecular Weight Melamine-Urea-formaldehyde Resin Impregnation on Poplar Wood Pore Size Distribution and Water Sorption

Effect of Impregnation with Maltodextrin and 1,3-Dimethylol-4,5-dihydroxyethyleneurea on Poplar Wood

Influence of Post-Treatment and Drying Process on the Modification of Wood with Resin-Impregnation

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Improvement of Wood Properties by Composite of Diatomite and “Phenol-Melamine-formaldehyde” Co-Condensed Resin

The Influence of Impregnation Methods and Curing Conditions on the Physical and Multiscale Mechanical Properties of Furfurylated Bamboo

Nano-Silica/Urea-Formaldehyde Resin-Modified Fast-Growing Lumber Performance Study

Effects of High-Temperature Heat Treatment Modification by Impregnation on Physical and Mechanical Properties of Poplar

Modification of Poplar Wood Reforced by PF Resin

The Effect of Microwave Pretreatment on the Impregnation of Poplar Wood

Study of Mechanical Performance and Gluability of Modified Fast-growing Poplar Wood

Mechanical Behavior and Natural Durability of Fast-Growing Poplar Wood Modified by Chemical Treatment

Modification Mechanisms and Properties of Poplar Wood via Grafting with 2-Hydroxyethyl Methacrylate/N,N'-methylenebis(acrylamide) onto Cell Walls

Preparation Optimization of Enhanced Poplar Wood by Organic–Inorganic Hybrid Treatment via Response Surface Methodology

Wood modification with phenol urea formaldehyde (PUF) resin: the influence of wood species selection on the dimensional stability

Manufacturing and Characterization of Modified Wood with In Situ Polymerization and Cross-linking of Water-Soluble Monomers on Wood Cell Walls

Improved Water Repellency and Dimensional Stability of Wood via Impregnation with an Epoxidized Linseed Oil and Carnauba Wax Complex Emulsion

Study on the Effect of Acrylic Acid Emulsion on the Properties of Poplar Wood Modified by Sodium Silicate Impregnation