Effect of ZrMgMo3O12 content on the thermal expansion and dimensional stability of ZrMgMo3O12p/2024Al composites
Junrui Yang,Chaofan Yin,Jianjun Chen,Yangcheng Xu,Mingyu Han,Guopeng Zhang,Zhongxia Liu
DOI: https://doi.org/10.1007/s10853-024-10124-6
IF: 4.5
2024-09-11
Journal of Materials Science
Abstract:With an increasing temperature gradient, the internal stress in composites can cause many problems, such as the plastic yield of the matrix, fracture of the reinforcements, growth of pores in the matrix, and debonding of the interface. The reinforcement particularly affects the internal stress, considerably changing the various properties of the composites. ZrMgMo 3 O 12particle (p) /2024Al composites were fabricated using 5−30 vol. % of a near-zero expansion material, ZrMgMo 3 O 12 , as a reinforcement. This was achieved via high-energy milling followed by vacuum hot pressing. The influence of the ZrMgMo 3 O 12 content on the thermal expansion and dimensional stability of the composites was investigated. The results indicated that the large thermal mismatch stress between ZrMgMo 3 O 12 and 2024Al limited the addition of ZrMgMo 3 O 12 to the composites. The composites with 30 vol. % ZrMgMo 3 O 12 failed after solid solution treatment during water quenching. With increasing ZrMgMo 3 O 12 content from 5 to 20%, the coefficients of thermal expansion (CTEs) first decreased and then increased, whereas the dimensional stability of the composites first increased and then decreased. The composites with 10% ZrMgMo 3 O 12 had the lowest CTE of 11.3 × 10 –6 °C −1 from − 100 °C to 400 °C, and exhibited dimensional stability from room temperature (RT) to 400 °C.
materials science, multidisciplinary