Abstract:diameter of 0.5‐1 µm and length of 10‐30 µm. The aluminum matrix composite reinforced by both β-eucryptite particles and aluminum borate whiskers ((Euc + ABO)/AA6061) was fabricated by a squeeze casting technique. The total volume fraction of β-eucryptite particles and aluminum borate whiskers was 40%, and the volume ratio between β-eucryptite and aluminum borate was 2:1. The pressure for squeeze casting was 30 MPa. The casting temperature of AA6061 was 800 ◦ C and the die temperature was about 520 ◦ C. In order to compare the properties of (Euc + ABO)/AA6061 with those of other materials, the composites reinforced by aluminum borate whiskers and silicon carbide whiskers were also fabricated on the above condition. The volume fractions of the reinforcements in the two composites were 25%. Tensile specimens were cut from the squeezing composite ingot. The tensile test was carried out on a CSS4400 tensile machine. The dimension of the specimens for the CTE measurement is φ 5m m× 18 mm. The CTE curve was measured on a Netzch DIL 401C Dilatometer with a heating rate of 8 ◦ C/min. The microstructure was examined by an Olympas PMG3 type optical microscope (OM). The OM photograph of the (Euc + ABO)/AA6061 composite is shown in Fig. 1. It can be seen that the distribution of β-eucryptite particles and aluminum borate whiskers in the composite are random and homogeneous. The comparison of the tensile strengths of the various materials is given in Fig. 2, which includes (Euc + ABO)/AA6061, AA6061, AA6061 matrix composites

Effect of interfacial reaction on the thermal expansion behavior of β-eucryptite particle and aluminum borate whisker reinforced 6061 aluminum alloy composite

Thermal expansion behavior and thermal mismatch stress of aluminum matrix composite reinforced by β-eucryptite particle and aluminum borate whisker

Microstructure and interfacial reactions of β-eucryptite particles in aluminum matrix composites

A study on an aluminum matrix composite reinforced by both β-eucryptite particle and aluminum borate whisker

Aluminum matrix composite with eucryptite particle and aluminum borate whisker

Abnormal thermal expansion behavior of aluminum borate whisker reinforced aluminum composite containing Fe3O4 particles

Effect of thermal exposure on interface and tensile properties of aluminum borate whisker reinforced pure aluminum composite

Thermal Expansion Behavior of Al Hybrid Composite Reinforced with Aluminum Borate Whisker and Magnetic Ceramic Particle

New aluminum matrix composite with much lower coefficient of thermal expansion and higher strength

Effect of Interfacial Reaction on Fracture Behaviour of Aluminium Borate Whisker Reinforced Aluminium Composite

Effect of interfacial Bi2O3 coating on compressive deformation behavior of aluminum borate whisker-reinforced aluminum composite at elevated temperature

Effect of Thermal Mismatch Stress on Thermal Expansion Behaviors of Al<sub>18</sub>B<sub>4</sub>O<sub>33</sub>w/Al Composite Containing Fe<sub>3</sub>O<sub>4</sub> Particle

Effect of Changing Rate of Residual Stress on Thermal Expansion Behavior of Magnesium Borate Whisker-Reinforced Aluminum Composite

Effect of Fe3O4 particles on thermal expansion behavior of Al18B4O33 whisker reinforced aluminum composite

Metastable Phase of Β-Eucryptite and Thermal Expansion Behavior of Eucryptite Particles Reinforced Aluminum Matrix Composite

Thermal Expansion Behaviors of Znal2o4-Coated Aluminum Borate Whiskers Reinforced Aluminum Composites

Interfacial reaction of aluminum borate whisker reinforced Mg-10Gd-3Y-1Zn-0.4Zr (wt%) alloy matrix composite

Dynamic Observation of Phase Transformation of Β-Eucryptite Particles in Aluminum Matrix Composite

Effect of Bi2o3 Coating of Whisker on Thermal Expansion Behaviour of Aluminium Composite Reinforced by Aluminium Borate Whisker

Interfacial Reactions and Mechanical Properties of 6061al Matrix Composites Reinforced with Alumina-Coated Al18B4O33 Whiskers