Abstract:Kaolinite-urea intercalation complex was prepared using kaolinite as intercalation host and urea as intercalating agent. The kaolinite-urea intercalation complex was used as precursor to prepare exfoliated kaolinite by deintercalating urea molecules from the interlayers of kaolinite through ultrasonic treatment. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the as-prepared exfoliated kaolinite. A broad 001 diffraction of kaolinite with weak intensity showed the random orientation of kaolinite platelets. SEM micrograph confirmed the exfoliation of kaolinite particles with layer thickness of no more than 50 nm. The exfoliated kaolinite particles were used as filler to poly(ethylene-oxide)/LiClO4 (PEO/LiClO4) system to prepare PEO/kaolinite composites, with the aim to improve the ion conductivity and mechanical property of the PEO matrix. SEM, transmission electron microscopy (TEM), XRD and Fourier transform infrared spectroscopy (FTIR) were used to characterize the PEO/kaolinite composites. SEM and TEM micrographs exhibited a good dispersion of exfoliated kaolinite in PEO matrix. XRD results showed that the crystallinity of PEO was gradually decreasing with increased exfoliated kaolinite content. FTIR analysis indicated that the hydrogen bonding was formed between the oxygen atoms of PEO segments and the hydroxyl groups on kaolinite surface, and this interaction between PEO and kaolinite was beneficial to the decrease in crystallinity of PEO. In order to evaluate the effect of the exfoliated kaolinite on ion conductivity and mechanical property of PEO matrix, AC impedance measurement and mechanical test were carried out. The results indicated that the ion conductivity of the composites gradually increased with increased exfoliated kaolinite content and reached 6.0 x 10(-5) S/cm at filler concentration of 20 wt%. The formation of amorphous region around the exfoliated kaolinite was beneficial for the Li+ ion conduction in PEO matrix. When the exfoliated kaolinite content reached 10 wt%, the formed amorphous regions were connected to each other to form a network for the transport of Li+ in the interconnected amorphous regions, leading to a sharp increase in ion conductivity. Moreover, the prepared composites under different drying temperature exhibited different ion conductivity. The reason was attributed to the change of PEO crystallinity with drying temperature, and the change trend of the ion conductivity was consistent with that of PEO crystallinity. Under the drying temperature of 95 degrees C, the as-prepared composite possessed high ion conductivity (6.8 x 10(-5) S/cm). In addition, the Young's modulus and tensile strength of the composites were improved because of the introduction of the exfoliated kaolinite into EPO matrix. The composites showed the maximal increase of 256% and 121% in Young's modulus and tensile strength, i.e., to 165.1 MPa and 6.743 MPa respectively, compared to PEO/LiClO4 (46.3 and 3.047 MPa). Therefore, the exfoliated kaolinite was a promising filler to prepare PEO based polymer electrolyte.

Research Progress and Prospect on the Intercalation and Exfoliation Technology of Kaolin

Kaolin Filling and Hand-Sheet Property in Dual Polymer Retention System

Factors influencing permeability anisotropy of remolded kaolin

Facile One-Step Microwave-Assisted Modification of Kaolinite and Performance Evaluation of Pickering Emulsion Stabilization for Oil Recovery Application.

Study on Anisotropic Permeability Model for Mixed Kaolin-Montmorillonite Clays

Effect of Crystallinity of Kaolinite on Urea Intercalation and Layer Expansion

A Study on the Intercalation and Exfoliation of Illite

The Role of Exfoliated Kaolinite on Crystallinity, Ion Conductivity, Thermal and Mechanical Properties of Poly(ethylene Oxide)/kaolinite Composites

A Study on Calcinated Whitening Technology of Kaolin in Benxi Formation, Jiaozuo Area

Quantitative Evaluation of the Effects of Salt Concentration and pH on the Self-Assembly of Kaolin Nanoplatelets

Preparation and Characterization of Poly(ethylene-oxide)/Kaolinite Composite Electrolyte

Facile Selective and Diverse Fabrication of Superhydrophobic, Superoleophobic-Superhydrophilic and Superamphiphobic Materials from Kaolin.

Research Status of Clay Intercalation

Mechanistic Links Between Magnetic Nanoparticles and Recovery Potential and Enhanced Capacity for Crystal Violet of Nanoparticles-Coated Kaolin

Research Progress of Attapulgite's Application

Regulation of Reactivity of Calcined Ultrafine Kaolin Products

Study on the dispersion stability of kaolin in oil phase

Study on the Activity of Metakaolin Produced by Traditional Rotary Kiln in China

Insights on the intercalation mechanism of the coal-bearing kaolinite intercalation based on experimental investigation and molecular dynamics simulations

Development of Polymer/Kaolinite Nanocomposites

Industrial-scale extraction of high value-added kaolin from excavation waste: Demonstration from Xiamen, China