Improving the Mechanical Strength of Paper Sheets Made from Phosphorylated Fibers Through the Use of Forming Agents
Hamid Lamoudan,Lahbib Abenghal,François Brouillette,Hamid LamoudanLahbib AbenghalFrançois BrouilletteInnovations Institute in Ecomaterials,Ecoproducts and Ecoenergies (I2E3),Université du Québec à Trois-Rivières (UQTR),Trois-Rivières,Canada
DOI: https://doi.org/10.1080/15440478.2024.2332705
2024-03-26
Journal of Natural Fibers
Abstract:The fabrication of paper or cardboards sheets with phosphorylated pulp fibers has proven to be a difficult task using traditional papermaking techniques. This problem is mainly attributed to the very high anionic charge of phosphorylated fibers. In the present work, we propose the use of cationic polymers as a neutralizing agent to attenuate the detrimental effect of the very high anionic charge of phosphorylated fibers and to promote the formation of microflocs that can be agglomerated into a uniform sheet with sufficient strength. The results obtained show that using positively charged retention agents significantly improves the sheet formation. The Kaptra formation index (KFI) was reduced from 133 to 17, which is a very good value when compared to unmodified kraft pulp fibers, which have a formation index of 35. The addition of cationic polymeric additives during the preparation of phosphorylated fiber sheets resulted in an improvement of mechanical properties over unmodified kraft pulp fibers, especially for tensile energy absorption and elongation. This study demonstrates that the use of cationic retention agents reduces the impact of the charge of the phosphorylated fibers on the overall sheet quality. 用磷酸化纸浆纤维制造纸张或纸板已被证明是使用传统造纸技术的一项艰巨任务. 这个问题主要归因于磷酸化纤维的阴离子电荷非常高. 在目前的工作中,我们建议使用阳离子聚合物作为中和剂,以减弱磷酸化纤维的非常高的阴离子电荷的有害影响,并促进微生物群落的形成,这些微生物群落可以聚集成具有足够强度的均匀片材. 所获得的结果表明,使用带正电的保持剂显著改善了片材的形成. Kaptra形成指数(KFI)从133降低到17,与形成指数为35的未改性硫酸盐浆纤维相比,这是一个非常好的值. 在磷酸化纤维片材的制备过程中添加阳离子聚合物添加剂,与未改性的硫酸盐浆纤维相比,提高了机械性能,尤其是拉伸能量吸收和伸长率. 这项研究表明,阳离子保留剂的使用减少了磷酸化纤维的电荷对整体片材质量的影响.
materials science, textiles