Effects of modified kaolin adsorbents on sodium adsorption efficiency and ash fusion characteristics during Zhundong coal combustion
Hao Zhou,Yujian Xing,Mingxi Zhou
DOI: https://doi.org/10.1016/j.joei.2021.04.017
IF: 6.47
2021-01-01
Journal of the Energy Institute
Abstract:The high sodium content in Zhundong coal results in severe slagging, ash deposition, high-temperature corrosion, and particle emission problems during utilization. Kaolin is a common in-furnace additive for the removal of sodium and alleviation of such issues. In this study, a novel modification method, namely, intercalationexfoliation combined with acid leaching, was applied to improve sodium adsorption efficiency of kaolin, with kaolin modified by intercalation-exfoliation and raw kaolin as a comparison. With combustion experiments and alkali metal vapor adsorption experiments, the effects of surface modification, combustion temperature, and blending ratio of kaolin adsorbents on sodium adsorption efficiency as well as the temporal profiles of alkali metal vapor adsorption processes fitted by four adsorption kinetic models were obtained. Experimental results showed that kaolin modified by the novel method displayed the best sodium adsorption performance, whose alkali metal vapor adsorption process was mainly controlled by intra-particle diffusion. In contrast, controlling steps of raw kaolin and kaolin with intercalation-exfoliation were external mass transfer and chemisorption on the surface, respectively. Such results arised from the amorphous transformation of crystal structure, increased adsorption sites after dehydroxylation, generation of free active silica with inner surface partly destroyed by acid, and loose scaly structure with expanded pore volume. Lower combustion temperature and higher blending ratio of kaolin were favorable for sodium adsorption. It was also found that kaolin additive caused a decrease in ash fusion temperatures (AFTs), and such tendency could be alleviated to some extent by the novel modification method. The blending ratio of kaolin should be determined according to the slag discharge mode (solid/liquid) during combustion. Kaolin modified by the method of intercalation-exfoliation combined with acid leaching had the best performance concerning sodium adsorption capacity and alleviation of slagging tendency, implying a broad application prospect.