Manipulating the Interfacial Band Bending For Enhancing the Thermoelectric Properties of 1T′‐MoTe2/Bi2Te3 Superlattice Films
Cheng Zhang,Zhe Chen,Hui Bai,Weixiao Lin,Ming Yang,Min Hong,Fangyang Zhan,Sen Xie,Min Zhang,Ziwei Li,Zhaohui Wang,Yubo Luo,Junyou Yang,Rui Wang,Jinsong Wu,Hang Zhang,Qingjie Zhang,Wei Liu,Xinfeng Tang
DOI: https://doi.org/10.1002/smll.202300745
IF: 13.3
2023-04-29
Small
Abstract:Work function difference induces spontaneous charge donation and band bending at the interfaces of superlattices, which is the origin of modulation doping and energy filtering, leading to remarkably enhanced thermoelectric performances. This optimizing strategy is successfully elucidated in 1T′‐MoTe2/Bi2Te3 superlattices. Meanwhile, the rational manipulation of interfacial band bending via tuning the Te/Bi flux ratio further promotes thermoelectric performances. Interfacial charge effects, such as band bending, modulation doping, and energy filtering, are critical for improving electronic transport properties of superlattice films. However, effectively manipulating interfacial band bending has proven challenging in previous studies. In this study, (1T′‐MoTe2)x(Bi2Te3)y superlattice films with symmetry‐mismatch were successfully fabricated via the molecular beam epitaxy. This enables to manipulate the interfacial band bending, thereby optimizing the corresponding thermoelectric performance. These results demonstrate that the increase of Te/Bi flux ratio (R) effectively tailored interfacial band bending, resulting in a reduction of the interfacial electric potential from ≈127 meV at R = 16 to ≈73 meV at R = 8. It is further verified that a smaller interfacial electric potential is more beneficial for optimizing the electronic transport properties of (1T′‐MoTe2)x(Bi2Te3)y. Especially, the (1T′‐MoTe2)1(Bi2Te3)12 superlattice film displays the highest thermoelectric power factor of 2.72 mW m−1 K−2 among all films, due to the synergy of modulation doping, energy filtering, and the manipulation of band bending. Moreover, the lattice thermal conductivity of the superlattice films is significantly reduced. This work provides valuable guidance to manipulate the interfacial band bending and further enhance the thermoelectric performances of superlattice films.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology