Abstract:New Fe82-85B13-16Si1Cu1 amorphous alloys with low B content and high B/Si content ratios were synthesized by melt spinning for developing good soft magnetic and high strength materials. The crystallization occurs through two stages and the first-stage onset temperature increases from 673 K to 705 K with increasing B content, while the second-stage temperature remains nearly constant. The first and second stages are due to the precipitation of the α-Fe(Si) phase with a size of about 30 nm and the decomposition of the remaining amorphous phase to α-Fe(Si)+Fe3B+Fe2B, respectively. The Fe-based alloys exhibited good soft magnetic properties both in annealed amorphous and nanocrystallized amorphous+α-Fe(Si) phases. The saturated magnetic flux density, coercivity and permeability at 1 kHz are 1.7 T, 4.92 A/m and 7100, respectively, for the annealed amorphous 14B alloy and 1.74 T, 5.62 A/m and 10100, respectively, for the nanocrystallized 13B alloy. The Vickers hardness (H v) is 803–867 for the as-spun state and it increases with decreasing B content. The H v increases significantly by crystallization to α-Fe+amorphous phases and reaches 997–1550 for the alloys annealed at 693–763 K just before T x2. The ultrahigh H v is presumably due to the combination of fine nanoscale mixed phases, high volume fraction of α-Fe(Si) without internal defects and the enrichment of B into the remaining amorphous phase. Such ultrahigh H v has not been obtained for Fe-based amorphous and crystallized alloys before and the addition of 1%Cu is essential for the ultrahigh H v and the amorphous phase formation for the Fe-rich 85%Fe alloy. The new Fe-based alloys are encouraging as future soft magnetic and ultrahigh strength materials with low material cost.

First Principle Study on the Soft Magnetic Saturation Properties of the Fe80Si(18-2x)PxBxCu2 Amorphous Alloys

High-temperature Magnetic Properties of Fe-based Nanocrystalline Alloy

Improving the Amorphous Forming Ability and Magnetic Properties of FeSiBPCu Amorphous and Nanocrystalline Alloys by Utilizing Carbon

The complementary effects of Fe and metalloids on the saturation magnetization of Fe-based amorphous alloys

The Research of FeSiCP Soft Magnetic Amorphous Alloy

Soft magnetic properties of FeCoSiBC amorphous alloys with high saturation magnetization

Effect of P/B ratio on the thermal stability, soft magnetic properties and magnetostriction properties of Fe80B14−xPxSi5C1 amorphous alloys

Effect of Fe Content on the Soft Magnetic Properties of Fe-Rich FeSiBC Amorphous Alloy

Tailoring Soft Magnetic Properties of Fe-based Amorphous Alloys Through C Addition

Modulation of soft magnetic properties of Fe83B10P4C2Cu1 amorphous alloys by V addition and annealing treatment

The Effects of Si Substitution with C on the Amorphous Forming Ability, Thermal Stability, and Magnetic Properties of an FeSiBPC Amorphous Alloy

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Effects of the Substitution of B and C for P on Magnetic Properties of FePCB Amorphous Alloys

Advances in amorphous and nanocrystalline magnetic materials

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

Local Structure, Nucleation Sites and Crystallization Behavior and Their Effects on Magnetic Properties of Fe81Si X B10P8−xCu1 (x = 0~8)

Research Progress and Application Prospect of Fe-based Soft Magnetic Amorphous/nanocrystalline Alloys

Advances in amorphous and nanocrystalline materials

Correlation among the amorphous forming ability, viscosity, free-energy difference and interfacial tension in Fe–Si–B–P soft magnetic alloys

Nanocrystallization, good soft magnetic properties and ultrahigh mechanical strength for Fe82-85B13-16Si1Cu1 amorphous alloys