Effect of P/B ratio on the thermal stability, soft magnetic properties and magnetostriction properties of Fe80B14−xPxSi5C1 amorphous alloys

Q. Yan,L. L. Lu,F. G. Chen,Aditya Jain,Y. G. Wang

DOI: https://doi.org/10.1007/s10854-024-12236-w

2024-02-27

Journal of Materials Science Materials in Electronics

Abstract:This work emphases on the effect of P/B ratio in Fe 80 B 14− x P x Si 5 C 1 ( x = 0, 1, 2, & 3 at%) amorphous alloys on the thermal stability, soft magnetic characteristics, and magnetostriction properties. The addition of P in Fe 80 B 14− x P x Si 5 C 1 ( x = 0, 1, 2, & 3 at%) amorphous alloys has a significant positive influence on the GFA. The addition of P element enhances the resistance to crystallization of amorphous alloys and broaden the optimal annealing temperatures range. The coercivity ( H c ) of the Fe 80 B 14− x P x Si 5 C 1 ( x = 0, 1, 2, & 3 at%) amorphous alloys is reduced from 15.6 to 9.03 A/m. The Fe 80 Si 5 B 12 C 1 P 2 amorphous alloy exhibits excellent soft magnetic characteristics at the annealing temperature of 613 K for 3 min, with a B s of 1.59 T and H c of 3.8 A/m. Mössbauer spectroscopy have been used to investigate the origin of the variations in the B s and H c of the amorphous alloy after annealing. The saturation magnetostriction coefficient ( λ s ) of Fe 80 B 14− x P x Si 5 C 1 ( x = 0, 1, 2, & 3 at%) amorphous alloy decreases after P element doping and annealing treatment, which can be used to explain the change of H c .

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied