Abstract:Coating system(s) will be required for Nb-silicide based alloys. Alumina forming alloys that are chemically compatible with the Nb-silicide based alloy substrate could be components of such systems. The intermetallic alloys Nb1.45Si2.7Ti2.25Al3.25Hf0.35 (MG5) and Nb1.35Si2.3Ti2.3Al3.7Hf0.35 (MG6) were studied in the cast, heat treated and isothermally oxidised conditions at 800 and 1200 °C to find out if they are αAl₂O₃ scale formers. A (Al/Si)alloy versus Nb/(Ti + Hf)alloy map, which can be considered to be a map for Multi-Principle Element or Complex Concentrated Nb-Ti-Si-Al-Hf alloys, and a [Nb/(Ti + Hf)]Nb5Si3 versus [Nb/(Ti + Hf)]alloy map were constructed making use of the alloy design methodology NICE and data from a previously studied alloy, and were used to select the alloys MG5 and MG6 that were expected (i) not to pest, (ii) to form αAl₂O₃ scale at 1200 °C, (iii) to have no solid solution, (iv) to form only hexagonal Nb₅Si₃ and (v) to have microstructures consisting of hexagonal Nb₅Si₃, Ti₅Si₃, Ti₅Si₄, TiSi silicides, and tri-aluminides and Al rich TiAl. Both alloys met the requirements (i) to (v). The alumina scale was able to self-heal at 1200 °C. Liquation in the alloy MG6 at 1200 °C was linked with the formation of a eutectic like structure and the TiAl aluminide in the cast alloy. Key to the oxidation of the alloys was the formation (i) of "composite" silicide grains in which the Nb₅Si₃ core was surrounded by the Ti₅Si₄ and TiSi silicides, and (ii) of tri-aluminides with high Al/Si ratio, particularly at 1200 °C and very low Nb/Ti ratio forming in-between the "composite" silicide grains. Both alloys met the "standard definition" of high entropy alloys (HEAs). Compared with HEAs with bcc solid solution and intermetallics, the VEC values of both the alloys were outside the range of reported values. The parameters VEC,  and  of Nb-Ti-Si-Al-Hf coating alloys and non-pesting Nb-silicide based alloys were compared and trends were established. Selection of coating alloys with possible "layered" structures was discussed and alloy compositions were proposed.

Microstructure and Cyclic Oxidation Behavior of Silicide Coatings Prepared by Molten Salt on Nb–Based Alloys

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

Formation and oxidation behavior of refractory high-entropy silicide (NbMoTaW)Si2 coating

Synthesis and Characterization of Silicide Coating on Niobium Alloy Produced Using Molten Salt Method

Development and oxidation behavior of high entropy silicide (NbMoTaWV)Si2 coatings on NbMoTaWV alloy

Study on the Oxidation Behavior of TiB2-CeO2-Modified (Nb,Mo,Cr,W)Si2 Coating on the Surface of Niobium Alloy

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

Microstructure and Composition Evolution of a Fused Slurry Silicide Coating on MoNbTaTiW Refractory High-Entropy Alloy in High-Temperature Oxidation Environment

On the Microstructure and Isothermal Oxidation at 800 and 1200 °C of the Nb-24Ti-18Si-5Al-5Cr-5Ge-5Sn (at.%) Silicide-Based Alloy

A novel composite Si-Mo-Ti coating with Ti concentration gradient for Nb-Si based ultrahigh temperature alloy prepared by slurry sintering

Anti-Corrosion Coatings for Protecting Nb-Based Alloys Exposed to Oxidation Environments: A Review

Microstructure and oxidation resistant of Si–NbSi2 coating on Nb substrate at 800°C and 1000°C

Microstructures and Isothermal Oxidation of the Alumina Scale Forming Nb1.45Si2.7Ti2.25Al3.25Hf0.35 and Nb1.35Si2.3Ti2.3Al3.7Hf0.35 Alloys

Microstructure and High-Temperature Oxidation Resistance of Molybdenum Disilicide Coating

Microstructure and high-temperature oxidation resistance of MoSi2-ZrO2 composite coatings for Niobium substrate

Cyclic oxidation behavior of Nb/Mn/Si alloying beta-gamma TiAl alloys

Morphology and Structure of Mo(Si,Al)_2 High Temperature Oxidation Resistant Coating

Formation and properties of niobium silicide coatings on Nb-Ta alloy substrate

Environmental Resistant Coatings for High Temperature Mo and Nb Silicide Alloys

The microstructure and high-temperature oxidation resistance of Si-rich Mo-Si-B coatings prepared by ultrasonic vibration assisted laser cladding

Microstructural Characterization and Anti‐Oxidation Properties of Molybdenum Disilicide Coating on Niobium by Spent MoSi 2 ‐Based Materials