Transition Metal-Promoted LDH-Derived CoCeMgAlO Mixed Oxides as Active Catalysts for Methane Total Oxidation
Marius C. Stoian,Cosmin Romanitan,Katja Neubauer,Hanan Atia,Constantin Cătălin Negrilă,Ionel Popescu,Ioan-Cezar Marcu
DOI: https://doi.org/10.3390/catal14090625
IF: 3.9
2024-09-18
Catalysts
Abstract:A series of M(x)CoCeMgAlO mixed oxides with different transition metals (M = Cu, Fe, Mn, and Ni) with an M content x = 3 at. %, and another series of Fe(x)CoCeMgAlO mixed oxides with Fe contents x ranging from 1 to 9 at. % with respect to cations, while keeping constant in both cases 40 at. % Co, 10 at. % Ce and Mg/Al atomic ratio of 3 were prepared via thermal decomposition at 750 °C in air of their corresponding layered double hydroxide (LDH) precursors obtained by coprecipitation. They were tested in a fixed bed reactor for complete methane oxidation with a gas feed of 1 vol.% methane in air to evaluate their catalytic performance. The physico-structural properties of the mixed oxide samples were investigated with several techniques, such as powder X-ray diffraction (XRD), scanning electron microscopy (SEM) coupled with energy dispersive X-ray spectroscopy (EDX), elemental mappings, inductively coupled plasma optical emission spectroscopy (ICP-OES), X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction under hydrogen (H2-TPR) and nitrogen adsorption–desorption at −196 °C. XRD analysis revealed in all the samples the presence of Co3O4 crystallites together with periclase-like and CeO2 phases, with no separate M-based oxide phase. All the cations were distributed homogeneously, as suggested by EDX measurements and elemental mappings of the samples. The metal contents, determined by EDX and ICP-OES, were in accordance with the theoretical values set for the catalysts' preparation. The redox properties studied by H2-TPR, along with the surface composition determined by XPS, provided information to elucidate the catalytic combustion properties of the studied mixed oxide materials. The methane combustion tests showed that all the M-promoted CoCeMgAlO mixed oxides were more active than the M-free counterpart, the highest promoting effect being observed for Fe as the doping transition metal. The Fe(x)CoCeMgAlO mixed oxide sample, with x = 3 at. % Fe displayed the highest catalytic activity for methane combustion with a temperature corresponding to 50% methane conversion, T50, of 489 °C, which is ca. 40 °C lower than that of the unpromoted catalyst. This was attributed to its superior redox properties and lowest activation energy among the studied catalysts, likely due to a Fe–Co–Ce synergistic interaction. In addition, long-term tests of Fe(3)CoCeMgAlO mixed oxide were performed, showing good stability over 60 h on-stream. On the other hand, the addition of water vapors in the feed led to textural and structural changes in the Fe(3)CoCeMgAlO system, affecting its catalytic performance in methane complete oxidation. At the same time, the catalyst showed relatively good recovery of its catalytic activity as soon as the water vapors were removed from the feed.
chemistry, physical