Ethylene/1-Hexene Copolymer with Broadened Molecular Mass Distribution Obtained by Catalysis of TiCl_4/XROH/MgCl_2/Et_3Al

Hong Wang

2010-01-01

Abstract:The synthesis of copolymer with high comonomer incorporation and broadened molecular mass distribution from ethylene with 1-hexene catalyzed by co-catalyst TiCl4/XROH/MgCl2 and Et3Al is described.The influences of the catalyst system composition and the polymerization conditions on the behavior of ethylene/1-hexene copolymerization,the structure,molecular mass and molecular mass distribution(MMD) of the obtained copolymer have been discussed in detail.When the copolymerization was performed under the optimum conditions:n(Ti)∶n(Mg)=10∶1,n(XROH)∶n(MgCl2)=2.6∶1,n(Al)∶n(Ti)=100∶1,P=0.45 MPa,t=80 ℃,Time=2 h and the comonomer concentration in feed=0.25 mol/L,the catalytic activity reached 23.2 kg/g cat.The catalyst particle shape and the structure and properties of the ethylene/1-octene copolymer are characterized with 13C NMR,X-ray,SEM,WAXD,DSC and GPC.These results show that the catalytic activity,molecular mass distribution and higher 1-hexene incorporation were considerably improved when the multi-halogen alcohol(XROH) was added into the catalyst system.By adding XROH in the catalyst system made Ti mass fraction of the catalyst increased up to 4.8%;the molar ratio of MMD of the copolymer became broader,ranging from 15 to 20;1-hexene incorporation within the copolymer chain was higher,up to 5.1%.