Abstract:In this study, a method of preparing a Ni-P-nanoPTFE composite coating on the surface of GCr15 steel for spinning rings is proposed. The method incorporates a defoamer into the plating solution to inhibit the agglomeration of nano-PTFE particles and pre-deposits a Ni-P transition layer to reduce the possibility of leakage coating. Meanwhile, the effect of varying the PTFE emulsion content in the bath on the micromorphology, hardness, deposition rate, crystal structure, and PTFE content of the composite coatings was investigated. The wear and corrosion resistances of the GCr15 substrate, Ni-P coating, and Ni-P-nanoPTFE composite coating are compared. The results show that the composite coating prepared at a PTFE emulsion concentration of 8 mL/L has the highest concentration of PTFE particles (up to 2.16 wt%). Additionally, its wear resistance and corrosion resistance are improved compared with Ni-P coating. The friction and wear study shows that the nano-PTFE particles with low dynamic friction coefficient are mixed in the grinding chip, which gives the composite coating self-lubricating characteristics, and the friction coefficient decreases to 0.3 compared with 0.4 of Ni-P coating. The corrosion study shows that the corrosion potential of the composite coating has increased by 7.6% compared with that of the Ni-P coating, which shifts from −456 mV to a more positive value of −421 mV. The corrosion current reduces from 6.71 μA to 1.54 μA, which is a 77% reduction. Meanwhile, the impedance increased from 5504 Ω·cm2 to 36,440 Ω·cm2, which is an increase of 562%.

Study of (Ni-W)-ptfe Composite Electrodeposition

Tribological performance of Ni-W/PTFE composite coating via pulse electrodeposition

Electrochemical Preparation and Characterization of Ni–PTFE Composite Coatings from a Non-Aqueous Solution Without Additives

Research of electrodeposited RE-Ni-Fe-P-PTFE composite coating

Electrodeposition of RE-Ni-Fe-P-PTFE Composite Coating

Electrodeposition of Hierarchically Structured Superhydrophobic Ni-PTFE Composite Coating with Remarkable Corrosion Resistance, Chemical and Mechanical Stability

Influence of the bath pH value on the microstructure and properties of a novel electrodeposited Ni-W-Ti3C2TX composite coating

Preparation and characterization of Ni-P-Al2O3-PTFE nanocomposite coatings by unidirectional jet electrodeposition

Robust Ni/WC superhydrophobic surfaces by electrodeposition

Electrodeposition of Ni-WC composite coatings: formation, structure and properties

Design and fabrication of a stable Ni-PTFE-SiC superhydrophobic anticorrosive coating by electrodeposition

Preparation of a Ni-P-nanoPTFE Composite Coating on the Surface of GCr15 Steel for Spinning Rings via a Defoamer and Transition Layer and Its Wear and Corrosion Resistance

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Enhancing Wear and Corrosion Resistance of Electroless Ni-P Coatings in CO 2 -saturated NaCl Solution through Polytetrafluoroethylene Incorporation

Non-Cyanide Electrodeposited Ag–PTFE Composite Coating Using Direct or Pulsed Current Deposition

Electroless deposition of ternary Ni–P alloy coatings containing tungsten or nano-scattered alumina composite on steel

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Preparation and properties of Ni-W-P-TiO2 nanocomposite coatings developed by a sol-enhanced electroplating method

PTFE layer formation during brush electroplating of nickel

Electrodeposition of Ni-P composite coatings: A review