Abstract:La 1- x Ce x (NiCoMnAl) 5 alloy electrodes were treated by hot charging in alkaline aqueous solution containing potassium borohydride. The activation behavior, hydrogen diffusion coefficient, maximum discharge capacity, high rate discharge capability of these alloy electrodes are then tested. The surface morphology and elemental content were observed using a scanning electron microscope .The results showed that the pre treatments markedly improved the activation behavior and the charging capacity of the alloy electrode. Hot charging of the alloy electrode in alkaline aqueous solution containing potassium borohydride fully activated the electrode after the second charging discharging cycle with a high discharging capability of 85% at 900mA/g. The surface had many micro cracks with a hydrogen diffusion coefficient of about 3.23×10 -9 cm 2/s. The mechanism causing the surface modifications of the alloy electrode is also analyzed.

Surface Modification and Preparation Technique for La_(1- X) Ce_x (nicomnal)_5 Hydrogen Storage Alloy Electrode