Effect of Specimen Size on Creep Crack Growth Rate in Superalloys IN625 and IN783

Kun Zhang,Jian-Ping Tan,Shan-Tung Tu
DOI: https://doi.org/10.1016/j.engfracmech.2023.109707
IF: 5.4
2023-01-01
Engineering Fracture Mechanics
Abstract:To further clarify the relation between the intensity of specimen size effect on creep crack growth (CCG) rate and operative creep fracture mechanisms, CCG testing and mechanism observation were carried out for two superalloys IN625 and IN783. Results show that the CCG data of different specimen types for IN625 basically coincide at 650 degrees C. In contrast, strong specimen size effect was observed in IN783 at 560 degrees C, that is, the CCG rate increases with the increase in specimen thickness, producing the largest CCG ratio of approximately seven. The load-line displacement and fracture mechanism analyses indicate that the IN625 specimens failed in a ductile and intergranular manner, while the IN783 specimens in a brittle and intergranular manner. The present study suggests that the influence of creep fracture mechanisms should be considered in the characterization of the specimen size effect on CCG rate.
What problem does this paper attempt to address?