4F3/2→4I9/2 and 4F3/2→4I13/2 laser operations with a Nd:GdTaO4 crystal

Renpeng Yan,Yiping Zhou,Xudong Li,Yang Liu,Yugang Jiang,Wenming Yao,Fang Peng,Qingli Zhang,Renqin Dou,Jing Gao

DOI: https://doi.org/10.1016/j.optlastec.2020.106444

2020-11-01

Abstract:This study investigated the laser performance of a Nd:GdTaO4 crystal for the 4F3/2→4I9/2 and 4F3/2→4I13/2 transitions at 928 nm and 1328 nm, respectively. A 5-mm-thick, 1.4 at.% Nd:GdTaO4 crystal was used in the experiments, under a pump at 879 nm, directly into the 4F3/2 emitting level. At a 10 Hz pump repetition rate, the maximum pulse energy at 928 nm reached 35.7 mJ, with an optical-to-optical efficiency of ~19.3%. When the pump repetition rate increased to 100 Hz, the laser pulse energy decreased to 13.5 mJ; the laser beam was characterised by M2 factors of Mx 2 = 1.4 and My 2 = 1.8 for the Ox and Oy axis, respectively. The Nd:GdTaO4 crystal yielded laser pulses at 1328 nm with a maximum energy of 9.7 mJ for operation at 10 Hz repetition rate; the overall optical-to-optical efficiency amounted to ~5.2%. Increasing the pump repetition rate to 100 Hz reduced the laser pulse energy to 5.8 mJ; the laser beam M2 factors were Mx 2 = 1.2 and My 2 = 1.4.

optics,physics, applied

What problem does this paper attempt to address?

This paper aims to study the laser performance of Nd:GdTaO₄ crystals under the 4F₃/₂→4I₉/₂ and 4F₃/₂→4I₁₃/₂ energy - level transitions, especially the laser operations at the wavelengths of 928 nm and 1328 nm. Specifically, the paper explores the following points:

1. **Laser performance**: Through experimental design, the laser output characteristics of Nd:GdTaO₄ crystals under these two energy - level transitions were studied, including factors such as maximum pulse energy, optical efficiency and beam quality.

2. **Pumping conditions**: The Nd:GdTaO₄ crystals were directly pumped by 879 nm laser diodes (LDs) with pumping repetition frequencies of 10 Hz and 100 Hz respectively, and the changes in laser performance under different pumping conditions were studied.

3. **Spectral characteristics**: The fluorescence spectra of Nd:GdTaO₄ crystals near 920 nm were measured by a spectral analyzer, and it was determined that the main emission peaks were located at 928 nm and 1328 nm.

4. **Influence of thermal effects**: The influence of thermal effects on laser performance was discussed, especially at high repetition frequencies, where thermal effects lead to a decrease in laser output energy and a deterioration in beam quality.

5. **Internal losses**: The internal losses of Nd:GdTaO₄ crystals were analyzed, and it was pointed out that this is one of the main factors affecting laser efficiency.

6. **Optimization suggestions**: Suggestions for improving the laser performance of Nd:GdTaO₄ crystals at the wavelengths of 928 nm and 1328 nm through improving crystal technology and parameter optimization were proposed.

In summary, the problem that this paper attempts to solve is: how to optimize the laser performance of Nd:GdTaO₄ crystals at the wavelengths of 928 nm and 1328 nm through experimental research and theoretical analysis, especially to increase their output energy and optical efficiency while improving beam quality.