Optical Spectroscopy of Nd3+/Mg2+co-doped LiTaO3laser Crystal

P. X. Zhang,Y. Hang,J. Gong,C. C. Zhao,J. G. Yin,L. H. Zhang,Y. Y. Zhu

DOI: https://doi.org/10.1088/1054-660x/23/1/015803

IF: 1.2

2012-01-01

Laser Physics

Abstract:A Nd3+ and Mg2+ co-doped LiTaO3 single crystal has been grown successfully by the Czochralski method. The polarized absorption spectra of the crystal were measured and investigated. The peak absorption cross-sections at 806 and 810 nm were 4.17 x 10(-20) cm(2) and 4.47 x 10(-20) cm(2) with a full width at half maximum of 29 and 17 nm for sigma- and pi-polarization, respectively. Based on the Judd-Ofelt theory, the spectral parameters of Nd3+ in the as-grown crystal were investigated in detail. Moreover, the emission probabilities, branching ratio and radiative lifetime for the transitions from F-4(3/2) were calculated. The radiative lifetime of F-4(3/2) was calculated to be 159 mu s and the luminescent quantum efficiency of the F-4(3/2) manifold was about 81.13%. The results were also compared with other Nd3+ doped crystals.