Gui-Hua Sun,Qing-Li Zhang,Jian-Qiao Luo,Xiao-Fei Wang,Chang-Jiang Gu,,
DOI: https://doi.org/10.7498/aps.73.20231362
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:In order to explore and develop new crystal materials in the 2.7—3 μm band, Pr, Yb, Ho:GdScO 3 crystal are successfully grown by the Czochralski method for the first time. X-ray diffraction measurement is performed to obtain powder diffraction data. Raman spectra aree measured and the vibration peaks are identified. The transmission spectrum, emission spectrum and fluorescence lifetime of Pr, Yb, Ho: GdScO 3 crystal are also characterized. The center of the strongest absorption band is at 966 nm with a half-peak width of 90 nm, which comes from the transition of Yb 3+ : 2 F 7/2 → 2 F 5/2 . The absorption cross section of Yb 3+ is calculated and the values at 966, 973, 985 nm are 0.62×10 –20 , 0.60×10 –20 and 0.58×10 –20 cm 2 respectively. The maximum emission peak is at 2850 nm and the half-peak width is 70 nm, the lifetimes of Ho 3+ : 5 I 6 and 5 I 7 are measured to be 1094 μs and 56 μs respectively, and the emission cross section at 2850 and 2935 nm are calculated to be 3.6×10 –20 cm 2 and 1.21×10 –20 cm 2 , respectively. Comparing with Yb, Ho: GdScO 3 crystal, the absorption peak of Yb 3+ and the emission peak are both broadened, which are related to the increase of crystal disorder. The lifetime of the lower energy level decreases significantly. Furthermore, the energy transfer mechanism between Ho 3+ and Pr 3+ is analyzed, and the energy transfer efficiency between Ho 3+ : 5 I 7 and Pr 3+ : 3 F 2 + 3 H 6 is calculated to be 99%, which is higher than those in other materials. All the results show that Pr, Yb, Ho:GdScO 3 crystal is an excellent 2.7–3 μm laser material, and is easier to achieve laser output than Yb, Ho:GdScO 3 crystal.
physics, multidisciplinary