Tm<SUP>3+</SUP>-doped calcium lithium tantalum gallium garnet (Tm:CLTGG): novel laser crystal
Adrian Alles,Zhongben Pan,Pavel Loiko,Josep Maria Serres,Sami Slimi,Shawuti Yingming,Kaiyang Tang,Yicheng Wang,Yongguang Zhao,Elena Dunina,Alexey Kornienko,Patrice Camy,Weidong Chen,Li Wang,Uwe Griebner,Valentin Petrov,Rosa Maria Sole,Magdalena Aguilo,Francesc Diaz,Xavier Mateos
DOI: https://doi.org/10.1364/OME.435238
2021-01-01
Optical Materials Express
Abstract:We report on the development of a novel laser crystal with broadband emission properties at similar to 2 mu m - a Tm3+, Li+-codoped calcium tantalum gallium garnet (Tm:CLTGG). The crystal is grown by the Czochralski method. Its structure (cubic, sp. gr . la (3) over bard, a = 12.5158(0) angstrom) is refined by the Rietveld method. Tm:CLTGG exhibits a relatively high thermal conductivity of 4.33 Wm(-1) K-1. Raman spectroscopy confirms a weak concentration of vacancies due to the charge compensation provided by Li+ codoping. The transition probabilities of Tm3+ ions are determined using the modified Judd-Ofelt theory yielding the intensity parameters Omega(2) = 5.185, Omega(4) = 0.650, Omega(6) = 1.068 [10(-20) cm(2)] and alpha = 0.171 [10(-4) cm]. The crystal-field splitting of the Tm3+ multiplets is revealed at 10 K. The first diode-pumped Tm:CLTGG laser generates 1.08 W at similar to 2 mu m with a slope efficiency of 23.8%. The Tm3+ ions in CLTGG exhibit significant inhomogeneous spectral broadening due to the structure disorder (a random distribution of Ta5+ and Ga3+ cations over octahedral and tetrahedral lattice sites) leading to smooth and broad gain profiles (bandwidth: 130 nm) extending well above 2 mu m and rendering Tm:CLTGG suitable for femtosecond pulse generation. (C) 2021 Optical Society of America under the terms of the OSA Open Access Publishing Agreement