Abstract:Microstructure, texture evolution and mechanical properties of extruded Mg-4.58Zn-2.6Gd-0.18Zr alloy were investigated at extrusion temperatures of 260 °C, 280 °C and 300 °C, extrusion ratios of 10, 15 and 30, and ram speeds of 3 mm s−1 and 6 mm s−1, respectively. The results indicated that the as-cast experimental alloy was composed of α-Mg matrix, coarse α-Mg + W(Mg3Zn3Gd2) eutectic and icosahedral quasicrystalline I(Mg3Zn6Gd) phase. A small amount of undissolved W phases were detected after the homogenization treatment at 505 °C up to 16 h, while most I phase dissolved into the α-Mg matrix. The initial crystallites before extrusion were randomly oriented, and showed a typical random texture. After extrusions, all samples exhibited a bimodal microstructure consisting of fine Dynamic recrystallization (DRX) grains and coarse elongated un-DRX grains, and the formation of ultra-fine DRX grains only occurred in the sample with an extrusion ratio of 10 at 260 °C, 3 mm s−1, which was caused by the solute segregation in homogenized billets and non-uniformly distributed W phase during the extrusion process. A fiber texture with {0002} planes and <1̄21̄0> directions paralleled to the extrusion direction was observed to be dominant in all the extruded samples. Furthermore, the increase of extrusion ratio was found to be beneficial for the DRX process and refinement of grain size, and the maximum texture intensity was accordingly weakened, which resulted in a decrease of tensile yield strength but an increase of elongation. With increasing the extrusion temperature or ram speed, both the grain size and DRX fraction gradually increased. Consequently, the texture was randomized and the maximum texture intensity decreased, which led to a reduction of the elongation and tensile yield strength. The tensile failure behaviors under different extrusion conditions were found to be related with the contraction twin lamellas formed in the un-DRX grains and the string-like W phases.

Uncovering of the Formation of Rare Earth Texture and Pseudo Fiber Bimodal Microstructure in the High Ductility Mg-2Gd-0.4Zr Alloy During Extrusion

Quasi-in-situ Observing the Rare Earth Texture Evolution in an Extruded Mg-Zn-Gd Alloy with Bimodal Microstructure

Correlation Between Dynamic Recrystallization and Formation of Rare Earth Texture in a Mg-Zn-Gd Magnesium Alloy During Extrusion

Analysis of Abnormal Texture and Strengthening Mechanisms of Extruded Mg–Gd–Y–Nd–Zr Alloy

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy

On the Origin of Non-Basal Texture in Extruded Mg-RE Alloys and Its Implication for Texture Engineering

Unveiling the Formation of Basal Texture Variations Based on Twinning and Dynamic Recrystallization in AZ31 Magnesium Alloy During Extrusion

Formation Mechanism of the Abnormal Texture During Extrusion in Mg-Y-Sm-Zn-Zr Alloy

Microstructure Evolution and Mechanical Properties of the Mg-Sm-Gd-Zn-Zr Alloy During Extrusion

Texture, microstructure and mechanical properties of an extruded Mg-10Gd-1Zn-0.4Zr alloy: Role of microstructure prior to extrusion

Microstructure and Texture Evolution of Mg-Gd-Y-Zr Alloy during Reciprocating Upsetting-Extrusion

Non-Basal Slip Induced Rare Earth Texture Evolution in Mg-14Gd-0.5Zr (wt.%) Alloy During the Traditional Hot Rolling

Effects of the Extrusion Parameters on Microstructure, Texture and Room Temperature Mechanical Properties of Extruded Mg–2.49Nd–1.82Gd–0.2Zn–0.2Zr Alloy

Effects of the Extrusion Temperature on Microstructure, Texture Evolution and Mechanical Properties of Extruded Mg-2.49Nd-1.82Gd-0.19Zn-0.4Zr Alloy

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Influence of Extrusion Conditions on Microstructure and Mechanical Properties of Mg-2Gd-0.3Zr Magnesium Alloy

On the Role of Yttrium in Microstructure Evolution and Texture Modification During Magnesium Alloy Extrusion

Improving the Isotropy and Formability of Extruded Mg-2Gd-1Zn (wt.%) Alloy Sheet by Introducing an Ellipse Texture

Texture role in the mechanical property improvement contributed by grain refinement for Mg-2.6Nd-0.55Zn-0.5Zr alloy subjected to extrusion process

Microstructure and Mechanical Properties of Extruded Mg-Gd-Y-Zn-Zr Alloys Filled with Intragranular LPSO Phases

Dynamic Recrystallization and Texture Evolution of Mg–Y–Zn Alloy During Hot Extrusion Process