Failure Analysis of Cold Rotary Swaging Die

Tiantai Tian,Hongtu Xu,Wenbin Zhan,Yu Zhang,Qi Zhang

DOI: https://doi.org/10.1016/j.engfailanal.2023.107580

IF: 4

2023-01-01

Engineering Failure Analysis

Abstract:Failure analysis was carried out on a cold rotary swaging die for batch production of small shafts and tubes. Characteristics of top and bottom surfaces were examined. Hardness distribution on the cross section and microstructure were analyzed. Stress distribution and wear on the die during rotary swaging were investigated by finite element analysis (FEA). The study showed that the internal damage, phase inhomogeneity, concentrated forming stress were the main three reasons for premature failure of the die. The internal damage caused the tensile strength to reduce by more than 55%. The content of 33.55% martensite near the arc surface was not high enough to prevent the cracks from propagating inward. The stress concentration at the bottom of the arc surface further decreased the bearing ability. Increasing the fillet angle can decrease the high stress by around 60% at the transition area and improving surface design can disperse the high stress area while reducing maximum stress by more than 35%.