Abstract:(Fe3-xMnx)(1-delta)O-4 was synthesized using a co-precipitation method and then developed as a catalyst for the low temperature selective catalytic reduction (SCR) of NO with NH3. The SCR activity of (Fe3-xMnx)(1-delta)O-4 was clearly enhanced with the increase of Mn content. The results of in situ DRIFTS study demonstrated that both the Eley-Rideal mechanism (i.e. reaction of activated ammonia with gaseous NO) and the Langmuir-Hinshelwood mechanism (i.e. reaction of adsorbed ammonia species with adsorbed NOx species) might happen during the SCR reaction over (Fe3-xMnx)(1-delta)O-4. According to the kinetic analysis, the respective contribution of the Langmuir-Hinshelwood mechanism and the Eley-Rideal mechanism on the SCR reaction was studied. Only the adsorption of NO + O-2 on (Fe2.8Mn0.2)(1-delta)O-4 was promoted, so the Langmuir-Hinshelwood mechanism predominated over NO conversion on (Fe2.8Mn0.2)(1-delta)O-4 especially at lower temperatures. Both the adsorption of NO + O-2 and the adsorption of NH3 on (Fe2.5Mn0.5)(1-delta)O-4 were obviously promoted, so NO conversion on (Fe2.5Mn0.5)(1-delta)O-4 mainly followed the Eley-Rideal mechanism especially at higher temperatures. Both the nitrate route and the over-oxidization of adsorbed ammonia species contributed to the formation of N2O on (Fe2.8Mn0.2)(1-delta)O-4 above 140 degrees C. However, the formation of N2O on (Fe2.5Mn0.5)(1-delta)O-4 mainly resulted from the over-oxidization of adsorbed ammonia species. Although the activity of (Fe2.5Mn0.5)(1-delta)O-4 was suppressed in the presence of H2O and SO2. the deactivated catalyst can be regenerated after the water washing. (C) 2011 Elsevier B.V. All rights reserved.

NO Catalytic Reduction on Urea-Loaded Ferromanganese Catalysts: Performance, Characterization, and Mechanism

Highly Efficient Fe-Cu/CL Catalysts Based on Low-Cost Clay Minerals for NH3-SCR of NOx at Low Temperature

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Removal of NO at low temperature and in the absence of ammonia over spherical activated carbon loaded with MnOx-CeO2 and urea

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Selective Catalytic Reduction of NO with NH3 over Mn–Fe/USY under Lean Burn Conditions

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Optimization of Robust FeMnSmO x Catalyst for Low-Temperature (<150 °C) NH 3 –SCR of NO x

Fe Promotion Effect in Mn/Usy for Low-Temperature Selective Catalytic Reduction of No with Nh3

Optimization of Robust FeMnSmOx Catalyst for Low-Temperature (<150 °C) NH3–SCR of NOx

[Reaction of NO with metal oxides and urea supported on activated carbons at low temperature]

Molecular-Level Insight into Selective Catalytic Reduction of NOx with NH3 to N2 over a Highly Efficient Bifunctional Va-MnOx Catalyst at Low Temperature

Design of a dual-bed catalyst system with microporous carbons and urea-supported mesoporous carbons for highly effective removal of NOx at room temperature

Selective catalytic reduction of no with urea supported on pitch-based spherical activated carbon at low temperatures

Iron Oxide-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOxwith NH3

Efficient FeMn/Al2O3 catalyst for NH3-SCR of NO at low temperature: the Influence of Strong Interactions Between Active Components and Carrier

Iron oxide-based catalysts for low-temperature selective catalytic reduction of NOx with NH3

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures

Low-Temperature Reduction of NOx by NH3 with Unity Conversion on Nanofilament MnO2/Activated Semi-Coke Catalyst

Removal of NOx using novel Fe-Mn-Ti compound catalysts at low temperature