Abstract:This study investigates the preparation of TiO2-SiO2-CaCO3 composite opacifier (Ti-Si-Ca) and its application in sanitary ceramic glazes. This approach involved hydrophobic agglomeration through surface-induced hydrophobic modification of TiO2, SiO2 and CaCO3 particles, along with the interactions between the hydrophobic carbon chains of modifiers. The Ti-Si-Ca formed a uniform coating with well-dispersed TiO2 and SiO2 particles on the CaCO3 surface and strong bonds formed among TiO2, SiO2 and CaCO3 through interpenetration of the organic carbon chains on the surface. The Ti-Si-Ca was added to the basic glazes of sanitary ceramics at a proportion of 15.5% and fired at 1125°C for 4 h. The resulting white ceramic glazes had chromaticity values of L*, a*, and b* at 93.76, -0.73, and 3.89, respectively, demonstrating superior glaze opacity and whiteness compared to glazes made with a ZrSiO4 opacifier (L* 90.30, b* 4.50). Glass and titanite phase make up the majority of the Ti-Si-Ca ceramic glazing layer of, with titanite serving as the opacified phase. Elimination of organic groups in Ti-Si-Ca during glaze firing formed interfacial chemical bonds among TiO2, SiO2 and CaCO3, which facilitated the synthesis of titanite from the three components at high temperatures. The Ti-Si-Ca was a highly opaque glaze without yellowing because the organic groups of Ti-Si-Ca were removed and interfacial chemical bonds formed among the TiO2, SiO2 and CaCO3 in the low-temperature stage of glaze firing. This transformed the three phases into titanite at high temperature and eliminated free TiO2. The formation of rutile TiO2, which has a yellow hue, at high temperatures was inhibited. This study provides a novel approach for low-energy preparation of TiO2-SiO2-CaCO3 composite opacifiers and addresses the challenge of replacing ZrSiO4 with TiO2 in ceramic opacifiers.

Synthesis of sphene by TiO<sub>2</sub> combined with CaCO<sub>3</sub> and SiO<sub>2</sub> in solid phase and its application as ceramic opacifier

Solid-phase synthesis of perovskite using spent SCR catalyst and calcium carbonate and its application as ceramic opacifier

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of TiO2-SiO2-CaCO3 Composite Opacifier by Hydrophobic Agglomeration and Mechanism of Inhibiting Glaze Yellowing

A zirconium-free glaze system for sanitary ceramics with SiO2-CaCO3-TiO2 composite opacifier containing anatase: Effect of interface combination among SiO2, CaCO3 and TiO2

Diopside-Based Glass-Ceramics from Chrysotile Asbestos Tailing

Preparation of a CaCO3-TiO2 Composite Based Opaque Glaze: Insight into the Mechanism of Opacification and Glaze Yellowing Inhibition

Preparation and Application of Apatite-TiO<sub>2</sub> Composite Opacifier: Preventing Titanium Glaze Yellowing through Pre-Combination

Preparation and Application of Apatite–TiO2 Composite Opacifier: Preventing Titanium Glaze Yellowing through Pre-Combination

Influence of Ca3(PO4)2 on the Surface Morphology and Properties of a CaO-Al2O3-SiO2-Fe2O3-Based High Temperature Phase Reconstructed Complex

Development of Sapphirine Opaque Glazes for Ceramic Tiles

Synthesis of Perovskite by Solid-Phase Method with Metatitanic Acid and Calcium Carbonate and Its Pigment Properties Investigation

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

PREPARATION AND CHARACTERIZATION OF TiO2/SERICITE COMPOSITE MATERIAL WITH FAVORABLE PIGMENTS PROPERTIES

Foaming Inhibition of SiC-containing Porcelain Ceramics by Using Si Powders During Sintering

Effect of SiO2/TiO2 ratio on the crystallization behavior of CaO-TiO2-SiO2 glass-ceramic system for opaque white glaze

Preparation of porous Al2O3 ceramics with enhanced properties by SLS using Al2O3 poly-hollow microspheres (PHMs) coated with CaSiO3 sintering additive

Synthesis and Chromatic Properties of Zircon Encapsulated Ceramic Black Pigment with Carbon Sphere As Carbon Source

Formation mechanism of titania based opacified glaze with novel core-shell nanostructure

Fabrication of a Photocatalytic Ceramic by Doping Si‐, P‐, and Zr‐Modified TiO2Nanopowders in Glaze