Abstract:A comprehensive research project consisting of pilot-scale combustion testing and long-term laboratory corrosion study has been performed. A pilot-scale combustion facility was modified to enable burning of pulverized coals under the conditions typical for coal-fired utility boilers. Eight United States (U.S.) coals were selected for this investigation, with the test conditions for all coals set to have the same heat input to the combustor. In addition, the air/fuel ratio was controlled so that approximately 3% excess oxygen was attained in the combustion gas at the furnace outlet, a location equivalent to the furnace exit of commercial boilers. During each pilot-scale combustion test, extensive online measurements of the flue gas compositions were performed. In addition, deposit samples were collected at the same location for chemical analyses. This information characterized well the combustion environments adjacent to the superheaters and reheaters of utility boilers burning different U.S. coals. The gas and deposit compositions were then simulated in a series of 1000-hour laboratory corrosion tests in which the corrosion performances of different alloys were evaluated at 704oC (1300oF). Results of this laboratory study led to better understanding of the corrosion mechanisms operating on superheaters and reheaters in coal-fired boilers due to the mutual presence of sulfur and chlorine in coal. A new corrosion mechanism, i.e., “Active Sulfide-to-Oxide Corrosion Mechanism,” accounts for the rapid corrosion attack on low-alloy ferritic steels and lower-grade stainless steels resulting from the formation of iron chloride (FeCl2) vapor and associated cycling reactions. For higher alloys containing sufficient chromium, the attack is dominated by Hot Corrosion in the presence of a fused salt. In addition, two stages of the hot corrosion mechanism have been elucidated here in detail. The initiation of hot corrosion attack induced by molten sulfate may involve Stage 1 “acidic” fluxing and re-precipitation of the protective scale formed initially on the deposit-covered alloy surfaces, followed by Stage 2 Hot Corrosion dominated by “basic” fluxing and re-precipitation after the scale is locally penetrated by the fused salt.

High-temperature Corrosion Mechanism Analysis of 310S Alloy in Typical MSWI Flue Gas Environment at 460–580 °C

Review on High Temperature Corrosion of Flue Gas from MSW Incineration

Study of Corrosion Kinetic Measurement and Morphology Observation of Superheater Tube 12cr1mov Alloy in Simulated MSWI Flue Gas Containing Varied HCl or SO2 Concentrations

Chlorine-induced Gas-Solid coupled corrosion behaviors of tube materials in high steam parameter MSW incinerator

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

In-situ sampling investigation of deposition and corrosion of convective heating surfaces in a grate type municipal solid waste incineration plant: a case study

Effect of complex municipal solid waste incineration flue gas on the corrosion of various alloys at 550 °C

Fireside Corrosion Behaviors Of Super304h And Hr3c In Coal Ash/Gas Environment With Different So2 Contents At 650 Degrees C

Fireside Corrosion Behaviors of Super304H and HR3C in Coal Ash/Gas Environment with Different SO 2 Contents at 650 °C

High Temperature Corrosion Resistance of Different Commercial Alloys Under Various Corrosive Environments

High-Temperature Corrosion Mechanisms for Selected Iron and Nickel-Based Alloys Exposed to Sulfur and Chlorine-Containing Environments

High-temperature corrosion behaviours of nickel–iron-based alloys with different molybdenum and tungsten contents in a coal ash/flue gas environment

Corrosion characteristics of Fe, Ni and Ti based alloys near the critical point of water and during supercritical water gasification and oxidation of municipal sludge

Investigation on High-temperature Corrosion of Superheaters in Biomass Boiler

Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650 ℃

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Comparative investigation on thermal corrosion of alloy coatings in simulated waste incinerator environment

High-temperature corrosion data and mechanisms for T122, Super304H and HR3C after 15 years in 1000MW ultra-supercritical power plant

Analysis and Solution of High-temperature Corrosion for a 1000 MW Ultra-supercritical Boiler

Experimental Investigation of Corrosion Associated with Gaseous HCl in the Superheaters in a Biomass Boiler

High temperature corrosion mechanism of Ni-5W-6B-28Cr-13Al alloy in simulated MSW incineration environment