Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Enhancing Yield Strength and Ductility of Fe-Mn-C-xAl (x = 0, 3) High Manganese Steel by Cryogenic Rolling

Influence of banded ε-martensite and deformation twin on cryogenic toughness of Fe-Mn-xAl-C steel

Deformation microstructures as well as strengthening and toughening mechanisms of low-density high Mn steels for cryogenic applications

Microstructure and Mechanical Properties of Medium Mn Steel Containing 3%al Processed by Warm Rolling

Enhancement of Yield Strength by Chromium/Nitrogen Alloying in High-Manganese Cryogenic Steel

Investigation on the microstructural evolution and mechanical properties of partially recrystallized Fe-27Mn-10Al-1.4C steel

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Ultra-Fine Heterogeneous Microstructure Enables High Strength-Ductility in a Cold-Rolled Medium Mn Steel

Tailoring retained austenite and mechanical property improvement in Al–Si–V containing medium Mn steel via direct intercritical rolling

Achieving ultrahigh strength in binary Al-10Mg alloy through heavy cryogenic rolling

Enhanced mechanical properties of a Fe-Mn-Al-C austenitic low-density steel by increasing hot-rolling reduction

Tailoring the Microstructure to Enhance the Cryogenic Mechanical Properties of a Fe–34.5mn–0.04c Steel

Tuning mechanical behavior and deformation mechanisms in high-manganese steels via carbon content modification

Effect of Mn‐bearing dispersoids on tensile properties and recrystallization resistance of Al‐3Mg‐0.8Mn rolled alloy

Microstructure and Mechanical Properties of a Novel Cold Rolled Medium-Mn Steel with Superior Strength and Ductility

Heterogeneous Multi-Phase Grains Improving the Strength-Ductility Balance in Warm-Rolled Fe-18Mn-3Ti Steel

The combination of strength and cryogenic impact toughness in low carbon 5Mn–5Ni steel

Effect of hot/warm rolling on the microstructures and mechanical properties of medium-Mn steels

Microstructure evolution and tensile behaviour of a cold rolled 8 wt\% Mn medium manganese steel

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures