Abstract:Silicon carbide fiber-reinforced silicon carbide ceramic matrix composites（SiCf/SiC） used in aero-engines are damaged or even failed due to the oxidation and corrosion by high-temperature and high-speed combustion gases. In this work，the gas generation device was used to simulate the complex gas environment in the aircraft engine，and the aviation kerosene mixed with liquid oxygen fuel in a certain proportion was ignited to form a high-temperature and high-speed combustion gas to assess the material. The oxidation test for 10 h and thermal shock test for 1000 cycles in combustion gas environment at 1200 ℃ were conducted on SiCf/SiC composites respectively. And the protective effect of environmental barrier coating（EBC）on SiCf/SiC composites was investigated. Uniaxial tensile tests were conducted on SiCf/SiC composites and SiCf/SiC-EBC composites after combustion gas environment assessment，and their fracture and cross-section micro-morphologies were observed by scanning electron microscopy. The results show that no significant oxidation of fibers and interphases is found in SiCf/SiC composites and SiCf/SiC-EBC composites after oxidation for 10 h in combustion gas environment，and their uniaxial tensile strength decreases by less than 2%. After 1000 thermal shock cycles in combustion gas environment，multiple micro-cracks are formed and oxidative corrosion of the interfacial layer occurs inside the SiCf/SiC composites，and the uniaxial tensile strength decreases by 41.3%. The EBC coating can effectively protect the SiCf/SiC composites from oxidation and corrosion of high-temperature gas，and the uniaxial tensile strength of SiCf/SiC-EBC composites decreases by 16.6% after 1000 thermal shock cycles.

Mechanical properties degradation and microstructure evolution of 2D-SiCf / SiC composites in combustion gas environment

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Microstructural and mechanical evolution of SiCf/SiC composites in wet oxygen atmosphere above 1000 degrees C

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Stress-corrosion Behavior of SiCf/SiC under CMAS-wet-oxygen Environments

Behavior of Two-Dimensional C/SiC Composites Subjected to Thermal Cycling in Controlled Environments

Temperature-dependent oxidation kinetics and mechanical properties degradation of Cf/ZrB2-SiC composites

The Degradation Behavior of C/Sic Composites in Complex Environment

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

High-temperature tensile behavior of 3D SiC/SiC composites

Influence of High-Temperature Oxidation and Test Conditions on the Dynamic Mechanical Properties of 2.5D SiCf/SiCm Composites

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Failure behavior of SiC/SiC with BSAS-based EBC in gas combustion environment

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Mechanical properties and microstructure evolution of 3D C f /SiBCN composites at elevated temperatures

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Effect of Oxidation Time on Fracture Behavior of C/SiC Composites at 800 °C in Air

Thermal cycling behavior of Si/Yb2SiO5/LaMgAl11O19 TEBCs coated SiCf/SiC composites under burner rig tests