Abstract:To examine the solution loss reaction properties of cokes with Ca/Fe additives in a hydrogen-rich blast furnace, the solution loss reactions of cokes were performed using a CO2 (N2) carrier gas with various percentages (0–30%) of H2O vapor, and the effect of Ca/Fe additives on the Boudouard reaction (C + CO2 = 2CO) and water–gas reaction (C + H2O = CO + H2) of cokes in a H2O + CO2 atmosphere was studied by examining the content of CO and H2 in the off-gas. The results demonstrate that the coke reactivity has a positive linear relationship with the percentages of H2O vapor in H2O + CO2 and H2O + N2 atmospheres, and the fitting slope k could be used to characterize the rate constant for the solution loss reaction of cokes in H2O + CO2 and H2O + N2 atmospheres. The k value for the solution loss reaction of the coke in the H2O + CO2 atmosphere is smaller than that of the coke in the H2O + N2 atmosphere, which shows that there is a competition between the reactions of H2O and CO2 with cokes in the H2O + CO2 atmosphere. Furthermore, the experimental reactivities of coke are smaller than their theoretical reactivities in the H2O + CO2 atmosphere, and the difference between the experimental and theoretical reactivities of the basic coke (BC) is less than those of the cokes with Ca/Fe additives (BC + Ca, BC + Fe), which shows that the Ca/Fe additives affect the competitive relationship of the reactions of CO2 and H2O with coke. Two inhibition factors, \begin{document}$\alpha_{{\rm{CO}}_2/{\rm{H}}_2{\rm{O}}} $\end{document} and \begin{document}$\alpha_{{\rm{H}}_2{\rm{O}}/{\rm{CO}}_2} $\end{document}, are proposed to measure the degree of inhibition based on the difference in the k value for the cokes in H2O + CO2 and H2O + N2 atmospheres. The inhibition factor \begin{document}$\alpha_{{\rm{CO}}_2/{\rm{H}}_2{\rm{O}}} $\end{document} could quantitatively characterize the inhibition degree of CO2 on C + H2O reaction in the H2O + CO2 atmosphere, and the inhibition factor \begin{document}$\alpha_{{\rm{H}}_2{\rm{O}}/{\rm{CO}}_2} $\end{document} could quantitatively characterize the inhibition degree of H2O on the C + CO2 reaction in the H2O + CO2 atmosphere. The \begin{document}$\alpha_{{\rm{CO}}_2/{\rm{H}}_2{\rm{O}}} $\end{document} factors of BC, BC + Fe, and BC + Ca cokes are 0.260, 0.251, and 0.170, respectively, and the \begin{document}$\alpha_{{\rm{H}}_2{\rm{O}}/{\rm{CO}}_2} $\end{document} factors of BC, BC + Fe, and BC + Ca are 0.121, 0.217, and 0.263, respectively. The Ca/Fe additives in cokes reduce the \begin{document}$\alpha_{{\rm{CO}}_2/{\rm{H}}_2{\rm{O}}} $\end{document} factor and increase the \begin{document}$\alpha_{{\rm{H}}_2{\rm{O}}/{\rm{CO}}_2} $\end{document} factor, showing that Ca/Fe additives can attenuate the inhibition degree of CO2 on the C + H2O reaction and improve the activity of the C + H2O reaction, and the Ca additive has a greater impact on the competitive relationship between the reactions of CO2 and H2O with coke than the Fe additive. The catalytically active substances in Ca/Fe additives in cokes could be CaFe2O4 and Ca2Al2SiO7, and the difference in the existing states of Ca/Fe elements in cokes causes the difference in the catalytic effect of Ca/Fe additives on the solution loss reactions of cokes.

Effect of Ca/Fe Additives on Solution Loss Reactions of Cokes in H2O+CO2 Atmosphere

Effect of Ca/Fe additives on the serial reactions of coke and sinter with CO2

Catalytic Effect of Alkali Metals on the Gasification Dissolution Reaction and Deep Reaction Behavior of Metallurgical Cokes.

Theoretical insight into the competitive effect of CO2 and additive H2O in coke gasification

Optimization of Calcium Carbide Residue Utilization for Producing High‐quality Calcium Carbonate

Effects of Alkali Earth Metal Ca Adding Ways on Coke Solution Loss Reaction

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Application of High‐ and Low‐Reactivity Cokes in Hydrogen‐Rich Blast Furnaces

THE EFFECT OF HEAVY METAL CONTENT AND DECOKING ADDITIVES ON COKING PRODUCT DISTRIBUTION

Influence of Sodium on Coke Microstructure in Different Reaction Atmosphere

The solution-loss reaction of cokes with different reactivity and lump ores during reductive coupling

Effect of CO2 atmosphere on Ca-containing mineral transformation behaviors during a Ca dominated coal co-firing with a Si/Al dominated coal in oxy-fuel condition

Production of highly reactive cokes by adding alkali metals and alkaline earth metals and their effect mechanism

Study on solution loss reaction of high reactivity coke mixed with iron ore powders

Strength degradation mechanism of iron coke prepared by mixed coal and Fe2O3

Influence Mechanisms of Additives on Coal-based Reduction of Complex Refractory Iron Ore

Degradation Behavior of Coke Reacting with H2O and CO2 at High Temperature

Effect of Ca3(PO4)2 additive on the slagging behavior during the cofiring of high‐sodium coal and iron-rich coal

Effect of Mixed Charging of Nut Coke and Sinter on Hydrogen-Rich Smelting Process of Blast Furnace

Influence of Na2CO3 on combustion performance of civil clean coke

Impacts of Alkali or Alkaline Earth Metals Addition on Reaction Intermediates Formed in Methanation of CO2 over Cobalt Catalysts