Abstract:The currently used low carbon operation in blast furnaces (BFs) leads to a thin coke layer and deterioration in gas and liquid permeability. Previous studies have reported that coke breeze, formed by the graphitization of coke, is one of the main influences on gas and liquid permeability in the high-temperature zone of a BF. To investigate the influence of the graphitization of BF coke on its metallurgical properties, the degree of coke graphitization under different heating temperatures from 1100 to 1500℃ was investigated. The dependence of the degree of graphitization on coke reactivity index (CRI) and coke strength after reaction (CSR) was also studied. The relationship between different degrees of graphitization in coke and alkali metals was clarified. Finally, the micro-morphology of coke was inspected and analyzed. Results show that with increasing temperature, the degree of coke graphitization intensifies. With every 100℃ rise in heating temperature, the degree of coke graphitization increases 1.8 times, the value of the spacing of layers (d002) decreases by 2%, and the values of the layers diameter of microcrystalline structure (La) and the stack height (Lc) are improved by 3% and 15%, respectively. In addition, it is observed that the surface stomata of the coke decreases particularly the large pores, the mosaic structure decreases, the isotropic structure increases, and the degree of structural ordering increases. When the degree of graphitization intensifies, the CRI of the coke gradually decreases, the CSR gradually increases, the degree of coke degradation weakens, the formed large pores reduced, and the trend for pore wall damage is reduced. Moreover, the alkali metal plays a catalytic role in improving the CRI and decreasing the CSR. It is considered that the graphitized coke resists the destruction of the alkali metal and thus decreases the degree of coke degradation.

Effects of Alkali Earth Metal Ca Adding Ways on Coke Solution Loss Reaction

Influence of Sodium on Coke Microstructure in Different Reaction Atmosphere

Catalytic Effect of Alkali Metals on the Gasification Dissolution Reaction and Deep Reaction Behavior of Metallurgical Cokes.

Production of highly reactive cokes by adding alkali metals and alkaline earth metals and their effect mechanism

The Effect of CaO Content on Sorption Performance of Nano CaO Based CO2 Adsorbent

Optimization of Calcium Carbide Residue Utilization for Producing High‐quality Calcium Carbonate

Study on CO2 Absorption-Mineralization Characteristics of Mixed Amine Solution Coupled with CaO and Key Influencing Factors in Mineralization Process

Impacts of Alkali or Alkaline Earth Metals Addition on Reaction Intermediates Formed in Methanation of CO2 over Cobalt Catalysts

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Degradation Behaviors of Coke under Complex Solution Loss Conditions

Studies on effects of alkali-metal compound additives on CaO sulphation

The solution-loss reaction of cokes with different reactivity and lump ores during reductive coupling

Influence of alkali metal K on the gasification reaction of ferro-coke with CO2

Effects of Sodium Carbonate and Sodium Chloride Additives on Alkaline Fusion of Coal Fly Ash

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Influence of Na2CO3 on combustion performance of civil clean coke

Effect and mechanism of nano-Ca 10 (PO 4 ) 6 (OH) 2 additive on compressive strength of calcium aluminate cement at high temperature

Effect of Calcium Aluminate-Based Additive on Properties of Periclase-Carbon Refractories for Steel-Teeming Ladles

Effect of modified Ca-Al adsorbents on heavy metal fixation during co-combustion of coal and coconut shells: Experiments and simulations

Effect of CO2 atmosphere on Ca-containing mineral transformation behaviors during a Ca dominated coal co-firing with a Si/Al dominated coal in oxy-fuel condition

The Effect of Metallic Salt Additives on Calcium-Based Desulfurization in O_2-CO_2 Pulverized Coal Combustion