Effect of self-assemble macropores on high-temperature thermoelectric performance of CaMnO 3 ceramics

Sijie Tong,Ying Zhang,Guoxin Hu,Ruochen Yang,Jiayu Chen,Yuan Liu,Junzhan Zhang,Zongmo Shi

DOI: https://doi.org/10.1007/s10854-023-11228-6

2023-01-01

Abstract:Calcium manganate (CaMnO 3 ) is considered as a potential n-type oxide thermoelectric material. It is of great significance to improve thermoelectric properties of CaMnO 3 at high-temperature application field. In this work, the anisotropic plate-like CaMnO 3 templates were synthesized by molten salt method and the macroporous CaMnO 3 thermoelectric ceramics were sintered by Spark Plasma Sintering (SPS). The influence of sintering temperatures on the thermoelectric properties were explored. The self-assemble macropores were built up due to the epitaxial growth of the anisotropic plate-like CaMnO 3 templates along their respective orientation during the sintering process. The pore size of 8 μm reached at 1423 K. The electrical resistivity of 12.4 mΩ cm, Seebeck coefficient of − 229.7 μV/K, and power factor of 0.42 mW/(m⋅K 2 ) were obtained for the samples sintered at 1423 K. The complex interface formed by irregular macropores could scatter phonons effectively and then reduce thermal conductivity. Although the electrical resistivity increased due to the presence of macropores, the overall ZT value was improved, reaching 0.35 at 1073 K. Therefore, the study provided a new idea for the improvement of CaMnO 3 thermoelectric performance.