Influence of Ce Doping on the Microstructure and High-temperature Electrical Property of CaMnO3 Ceramics

Li-juan SUN,Cui-qin LI,Qian-lin CHEN,Dong-zhen ZHOU,Ya WEN,Jun LIU,Yu YAN

DOI: https://doi.org/10.3969/j.issn.1000-985X.2018.03.012

2018-01-01

Abstract:CaMnO3 has attracted increasing attention as one of the most promising n-type thermoelectric materials due to its natural abundance,low toxicity,high-temperature thermal and chemical stability.However,the thermoelectric properties of CaMnO3 were discouraging for its high electrical resistivity.High-valence rare earth doping at Ca site is an effective way to reduce the electrical resistivity.The Ca1-x Cex MnO3 (x =0,0.02,0.04,0.06,0.10) was synthesized using co-precipitation method and their electrical properties were investigated.The phase structure and microscopic morphology of all the samples was characterized by XRD and SEM.The electric resistivity and Seebeck coefficient were determined by four probe method.The results of XRD indicated that All the samples were single-phase orthorhombic perovskite structures at room temperature.SEM showed that the Ce doping samples possessed dense structure,smaller and evenly dispersed particle size.Increasing Ce concentration leads to a significant decrease in electrical resistivity and absolute value of Seebeck coefficient (｜ S ｜).The highest power factor of 2.76 × 10-4 W · m-1 · K-2 for Ca1-xCex MnO3 at 973 K is obtained.