Abstract:Twin grain boundaries (GBs) are found to be inherently resistant to stress corrosion cracking (SCC), which has become one of the main failure mechanisms of steam generator (SG) tubing since the 1980s and brings huge economic losses to the nuclear power plants. As it is a widely used material for SG tubing, the SCC-resistance of the twins in Alloy 690TT in 10 wt.% sodium hydroxide solution with 100 ppm litharge at 330 degrees C was studied using C-ring samples. The relationship between the crack paths, twin GBs and the residual strains in the studied areas were analyzed using an environmental scanning electron microscope (ESEM) equipped with electron backscatter diffraction (EBSD) equipment. A continuously stressed C-ring sample without immersion was used to evaluate the effect of residual stress or strain on the microstructure of the twin GBs. The oxides at the crack paths were analyzed by an energy dispersive spectroscopy (EDS). The results show that many twin GBs are cracked during crack propagation. There are more twins with large deviations from the ideal Sigma 3 twin misorientation in the studied area where the residual strain is high. In situ EBSD analyses verify that higher residual strain causes twins to deviate from the ideal twin microrientation and can even promote twins transiting into random high angle grain boundaries, when the residual strain is high enough. The EDS result illustrates that litharge accelerates the dissolution of the chromium and nickel in the matrix. Overall, the SCC-resistance of the twins in Alloy 690TT in the studied solution is reduced by the destruction of the ideal microrientation of the twin GBs and the preferential dissolution of chromium and nickel at the crack paths. Higher residual strain on the Alloy 690TT and deleterious impurities in the circulating secondary water should be eliminated during the operation of nuclear power plants. (C) 2011 Elsevier B.V. All rights reserved.

CORROSION BEHAVIOR OF ALLOY 690TT IN HIGH TEMPERATURE LEAD-CONTAINING CAUSTIC SOLUTION

Intergranular Attack and Intergranular Stress Corrosion Cracking of Alloy 690 TT in High Temperature Lead‐containing Caustic Solution

Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution

Corrosion Behavior of Alloy 690 in Aerated Supercritical Water

STRESS CORROSION CRACKING BEHAVIOR OF ALLOY 600 IN HIGH TEMPERATURE HIGH PRESSURE LEAD-CONTAINING CAUSTIC SOLUTION

Effects of Scratching on Corrosion and Stress Corrosion Cracking of Alloy 690TT at 58°C and 330°C

CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR

Effect of temperature on corrosion behavior of alloy 690 in high temperature hydrogenated water

Property of surface film of Alloy 690 in simulated primary water

EFFECTS OF Cl~- CONCENTRATION AND TEMPERATURE ON THE CORROSION BEHAVIOR OF ALLOY 690 IN BORATE BUFFER SOLUTION

Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution

High-Temperature Corrosion Behaviors of Structural Materials for Lead-Alloy-Cooled Fast Reactor Application

Stress Corrosion Behavior of Scratched Alloy 690TT Steam Generator Tube in Chlorine‐containing High‐temperature Pressurized Water

Trans-twins Stress Corrosion Cracking Behaviors of Alloy 690TT in Lead-Containing Caustic Solution at 330°C

Fretting Corrosion-Induced Microstructural Evolution of Alloy 690TT Tube in High Temperature Pressurised Water

Electrochemical corrosion behaviour of Alloy 690 in simulated PWR high temperature aqueous environments

Microstructural characteristics of the oxide films formed on Alloy 690 TT in pure and primary water at 325°C

Corrosion behavior of T91 steel in liquid lead-bismuth eutectic at 550 C: Effects of exposure time and dissolved oxygen concentration

Corrosion of Artificial Aged Magnesium Alloy AZ80 in 3.5 Wt Pct NaCl Solutions

MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING

Influence of Later-Dissolved Oxygen on Microstructural Changes in Oxide Films Formed on Alloy 690TT in Hydrogenated Primary Water