Abstract:Alloy 800 is extensively used in nuclear power plants (NPPs) as steam generator tubing material and is essentially the pressure barrier between radioactive and non-radioactive components of the heat transport system in a NPP. Alloy 800 tubes are subjected to various surface finishing operations such as shot peening, pickling and passivation, and electropolishing before installing it in nuclear plants. The finishing operations carried out could cause a significant change in surface conditions that may alter the high-temperature oxidation behavior of Alloy 800. Surface finishing operations such as electropolishing, pickling and passivation and shot peening were carried out on Alloy 800. Surface roughness was measured for different surface-treated samples by using laser profilometer. The residual stress on the treated surface was quantified using grazing incidence x-ray diffraction (Sin 2 Ψ method). The microhardness measurements were carried out to evaluate the effect of strain hardening. All of the surface-treated specimens along with the as-received specimen were exposed in steam environment in an autoclave at 400 °C, 10 MPa for a period of 72 h. The difference in color of oxide film correlated with weight change of specimen having different surface treatments. It was observed that surface roughness, residual stress and hardness of the surface influence the oxidation behavior. The oxidation was more in the presence of tensile residual stress compared to compressive residual stress on Alloy 800. The morphology, orientation and composition of oxide layer thus formed during exposure to high-temperature steam were characterized using scanning electron microscopy (SEM), microlaser Raman spectroscopy (MLRS). The oxide film formation rate varied on Alloy 800 due to different surface finishing operations. The oxide film morphology and composition plays an important role in localized corrosion resistance of Alloy 800. The oxide film instability would result in local breakage which acts as a precursor for stress corrosion cracking (SCC) initiation on Alloy 800. This study establishes the influence of surface treatments and the residual stress generated on high-temperature steam oxidation of Alloy 800.

A high-resolution characterization of surface film formed on alloys 800 and 690 exposed to chloride and thiosulfate-containing solution at 300°C

Property of surface film of Alloy 690 in simulated primary water

Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States

ANALYSES OF SURFACE OXIDE FILMS ON ELECTROPOLISHED ALLOY 690TT AFTER IMMERSION FOR DIFFERENT TIMES

CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR

Analyses of Surface Oxide Films on Ground Alloy 690tt after Immersion for Different Times

Preparation and Characterization of Α-Al2o3 Film by Low Temperature Thermal Oxidation of Al8Cr5 Coating

Microstructural characteristics of the oxide films formed on Alloy 690 TT in pure and primary water at 325°C

Influence of Dissolved Oxygen on Oxide Films of Alloy 690TT with Different Surface Status in Simulated Primary Water

The Microstructure of Aluminide Coatings on 310S and 347H Steels Formed by Pack Aluminizing and Their Corrosion Behavior in Molten Chloride Salts

Short-time Oxidation of Alloy 690 in High-temperature and High-pressure Steam and Water

The mechanism of oxide film formation on Alloy 690 in oxygenated high temperature water

Analyses of Oxide Films Grown on Alloy 625 in Oxidizing Supercritical Water

Systematic investigation of the oxidation behavior of Fe-Cr-Al cladding alloys in high-temperature steam

Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings

Influence of Later-Dissolved Oxygen on Microstructural Changes in Oxide Films Formed on Alloy 690TT in Hydrogenated Primary Water

High Temperature Oxidation of Alloy 617, 740, HR6W and Sanicro 25 in Supercritical Water at 650°C

Investigating the Impact of Surface Finishing and Residual Stress on the Oxidation Behavior of Alloy 800

Influence of Dissolved Oxygen Concentration on the Oxide Film Formed on Alloy 690 in High Temperature Water

Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution

Incipient Corrosion of FeCrAl Alloys in H3BO3- and LiOH-containing Pure Water at 360 °C and 18.5 MPa