Abstract:In order to improve the activation behavior of Ti1.02Cr1.1Mn0.3Fe0.6 alloy with high hydrogen desorption pressure for hybrid hydrogen storage vessel application, the rare earth (RE) doped Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 (RE = La, Ce, Ho) alloys were prepared by induction levitation melting. The effect of rare earth doping on the microstructures and hydrogen storage properties was also investigated systematically. The results show that Ti1.02Cr1.1Mn0.3Fe0.6 alloy displays a single C14 Laves phase, and there is a secondary phase of rare earth oxide in the RE doped alloys. The RE doping strategy can expand the unit cell volume of C14 Laves main phase. After RE doping, the activation behavior of the Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 alloy is obviously improved and the hydrogen storage capacity is increased, while the hydrogen desorption plateau pressure is decreased. Moreover, the RE-free alloy can hardly absorb hydrogen at room temperature under 34-43 MPa hydrogen pressure, but all RE-doped alloys can absorb hydrogen to saturation under the same condition. The decline of pressure plateau is inversely proportional to the atomic number of RE. Among the studied alloys, the Ti(1.02)Cr(1.1)Mn(0.3)Fe(0.6)La0.03 alloy shows the best overall properties and can be fully activated at room temperature. Its hydrogen absorption pressure is 39.31 MPa and 51.27 MPa under 298 K and 318 K, respectively. Its hydrogen storage capacity is up to 1.715 wt% and the dissociation enthalpy is 16.63 kJ/mol H-2 with a desorption plateau slope of 0.098. (C) 2017 Published by Elsevier B.V.

EFFECT OF Cr CONTENT ON THE SORPTION PERFORMANCE OF TiMn_(1.2-x)Cr_xV_(0.25)Fe_(0.05) ALLOYS

Effect of Cr Content on the Sorption Performance of Timn1.2-Xcrxv0.25fe0.05

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Effect of Rare Earth Doping on the Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Effect of Cr content on hydrogen storage properties for Ti-V-based BCC-phase alloys

Phase Structure and Hydrogen Sorption Performance of Ti–Mn-based Alloys

Hydrogen Storage Characteristics of TiMn1.25-5yCr0.25(V4Fe)y Alloys

Phase structures and hydrogen storage properties

Effect of Zr Content on the Microstructures and Hydrogen Storage Properties of (Ti-Cr)_(45-x)V_(55)Zr_x(x=1～7) Alloys

Influence of the Substitution Cr for Mn on Structural and Hydrogen Storage Performance of Ti 0.9 Zr 0.1 V 0.45 Cr X Mn 1.5-X (x=0, 0.05, 0.1, 0.15, 0.2) Alloys

Influence of Ti Super-Stoichiometry on the Hydrogen Storage Properties of Ti1+xCr1.2Mn0.2Fe0.6 (x = 0–0.1) Alloys for Hybrid Hydrogen Storage Application

Effects of Partial Substitution of Fe for Cr on Hydrogen Storage Performance of TiVCrMn Alloys

Effect of zr content on the microstructures and hydrogen storage properties of (Ti-Cr)(45-x)V55Zrx (x=1 similar to 7) alloys

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6-1.6) alloys

Dependence of Hydrogen Storage Capacity of TiCr1.8−X(VFe)X on V–Fe Content

Phase structures and electrochemical behaviors of V2.1TiNi 0.5Hf0.05Crx (x=0-0.152) hydrogen storage alloys

Influence of Annealing Treatment on the Microstructure and Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application