Abstract:Copper oxide was synthesis by hydrothermal method using copper nano powder (30nm) and deionized water on quartz substrate. At temperature 100 °C, different experimental time ranging from (24–72 h). Different copper oxide phase was presented in X-Ray diffraction analyzer, the crystal size increased as the reaction time increased as it calculated using scherrer equation to be (21.1–32.03 nm), and Williamson Hall plot to be (40.3–87.7 nm). Also, Raman spectroscopy show different copper phase and the highest intensity peak at 220 cm −1 , due to the cuprous oxide in all sample used to distinct chemical fingerprint for a particular molecule or material. Many of metal oxide bond was study by FTIR to clarify the compositional and chemical properties of the prepared samples. Optical characteristic with different absorption peaks of thin film show decrease in the band gap from (2.8–2.4 eV) as the reaction time increase. PL measurement used also to determine the band gap energy of the prepared thin film which found to be agreement with UV–Vis, and the band gap value is (2.7, 2.6, 2.5, 2.3, and 2.3 eV), respectively. Increasing in the surface roughness from (3.637–25.16 nm), and in the root mean square from (5–29.39 nm), and grain size with increasing the reaction time from (24–72 h), respectively, was measured by using AFM technique. Different morphologies were showed with increasing the reaction time, spherical and truncated octahedral in different type was obtained by field emission-scanning electron microscope (FE-SEM) as the particles subject to transformation caused the preparing agglomerated crystallites. The electrical characteristic was analysis use DC measurement to measure the activation energy which varied with reaction time. The figure of merit analysis shows that the copper oxidation state to obtain cuprous oxide (Cu 2 O) is mainly obtained at the 48 h-reaction time. The used of copper nano powder in hydrothermal method without adding any auxiliary material the main aim of this research.

Preparation of Nano Cuprous Oxide by Ball Milling in Water Solution

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Preparation of Cu2O Nanoparticles in Cupric Chloride Solutions with a Simple Mechanochemical Approach

Preparation of CuO Nanopowders by Ultrasonic Solid-liquid Reaction with Ball Milling

Preparation of Nano-particles of Metal Oxides by Wet Milling Process

Synthesis of Cuo Nanoparticles for Catalytic Application Via Ultrasound-Assisted Ball Milling

Study on Preparation of Copper Oxide Nanopowders

Preparation and Characterization of CuO Nanoparticles with Different Size and Morphology

Preparation of Cuprous Oxide Particles of Different Crystallinity

Deposition time effect on copper oxide nano structures, an analysis study using chemical method

Formation of Cu2O Solid Solution Via High-Frequency Electromagnetic Field-Assisted Ball Milling: the Reaction Mechanism

Preparation of Cu2O Hollow Nanospheres under Reflux Conditions

Preparation of Nanoscale CuO Powders

Preparation of Fe3O4 Nanoparticles by Ball Milling Iron Powder in Water Solution

Study on preparation of nano-Cu powders by hydrogen reducing

Morphology Control of Cuprous Oxide Micro-and Nanoparticles by Polyol Method

Preparation and Characterization of Cu Nano-Powders by Hydrothermal Decomposition and Hydrogen Reduction Process

Copper nanocubes and nanostructured cuprous oxide prepared by surfactant-assisted electrochemical deposition

SYNTHESIS AND PHOTOCATALYSIS OF CUPROUS OXIDE NANO-SPHERES IN AQUEOUS

Sonochemical Preparation of Micro- and Nanometer Cu2O

A novel wet-chemical method of preparing highly monodispersed Cu2O nanoparticles