Morphology Controllable Iron Oxide Synthesized from Pyrite Cinders by Hydrothermal Method

Yong Zheng

2011-01-01

Abstract:Iron oxide particles with different morphologies were synthesized by hydrothermal treatment using ferric hydroxide gel as precursor,prepared by adding ammonia to sulfuric acid leaching solution of pyrite cinders.In addition,the effects of reaction temperature,n(Fe2+)/n(Fe3+),total iron concentration and seed crystals adding amount on the phase,shape and size of the prepared iron oxide in the neutral medium were investigated.The phase and shape of the synthesized iron oxide particles were characterized by X-ray diffraction(XRD),scanning electron microscope(SEM),transmission electron microscopy(TEM) and selected area electron diffraction(SAED).The results show that platelet-type α-Fe2O3 particles are prepared via hydrothermal route when the temperature is 230 ℃,n(Fe2+)/n(Fe3+) is 0.1,total iron concentration is 1.25 mol/L and seed crystal adding amount is 2 g.With the increase of temperature,when it is in the range of 140?260 ℃,the hydrothermal products transfer from α-FeOOH to α-Fe2O3 and their shapes change from sphere to round pie and then to platelet.With the increase of n(Fe2+)/n(Fe3+),in the range of 0?0.12,the hydrothermal products are transferred from α-Fe2O3 to α-Fe2O3 and Fe3O4,and the shapes of α-Fe2O3 particles gradually change to platelet from sphere.Furthermore,the particle size also increases with the increase of n(Fe2+)/n(Fe3+).The obtained iron oxide particles become heterogeneous when the total Fe concentration is 0.625 mol/L,while it becomes sphere when the total Fe concentration is 1.875 mol/L.The products are elliptical without adding any seed crystal,while it becomes heterogeneous when the crystal seed adding amount is 6 g.